Описание материалов:
SABIC® PP QR674K is a high melt flow index random copolymer with excellent transparency and good antistatic properties. This grade combines improved aesthetics of the finished articles with low temperature processability and a very good organoleptic performance. Part aesthetics are not affected by the lower temperatures, providing for a broader operating window. The SABIC®PP QR674K presents excellent flow behaviour, easy demoulding and good stiffness to impact ratio.
SABIC® PP QR674K is mainly used in injection moulding processes. The SABIC® PP QR674K aims at transparent applications were higher MFI's with good flow are required. Its intended applications include injection moulded housewares, office & home storage boxes, thin wall packaging, lids and caps & closures.
The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications.
| Главная Информация | |
|---|
| Добавка | - Антистатический
- Осветитель
|
| Характеристики | - Антистатический
- Хорошая ударопрочность
- Хороший выпуск пресс-формы
- Хорошие органолептические свойства
- Хорошая технологичность
- Хорошая жесткость
- Высокая четкость
- Высокий поток
- Приятный внешний вид
- Случайный сополимер
|
| Используется | - Колпачки
- Затворы
- Контейнеры
- Товары для дома
- Крышки
- Тонкостенная упаковка
- Прозрачные детали
|
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Массовый расход расплава (MFR) (230°C/2.16 kg) | 40 | g/10 min | ASTM D1238, ISO 1133 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale) | 90 | | ASTM D785 |
| Твердость по суше (Shore D) | 64 | | ISO 868 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | | | |
| 1% Secant 1 | 1200 | MPa | ASTM D638 |
| -- | 1150 | MPa | ISO 527-2/1A/1 |
| Прочность на растяжение | | | |
| Yield 2 | 29.0 | MPa | ASTM D638 |
| Yield | 29.0 | MPa | ISO 527-2/1A/50 |
| Удлинение при растяжении | | | |
| Yield 3 | 13 | % | ASTM D638 |
| Yield | 13 | % | ISO 527-2/1A/50 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность | | | ISO 179/1eA |
| 0°C | 2.0 | kJ/m² | |
| 23°C | 4.5 | kJ/m² | |
| Зубчатый изод Impact | | | |
| 0°C | 25 | J/m | ASTM D256A |
| 23°C | 45 | J/m | ASTM D256A |
| 0°C | 2.0 | kJ/m² | ISO 180/1A |
| 23°C | 4.0 | kJ/m² | ISO 180/1A |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | |
| 0.45 MPa, Unannealed | 80.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 75.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 57.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 52.0 | °C | ISO 75-2/Af |
| Викат Температура размягчения | | | |
| -- | 125 | °C | ASTM D1525, ISO 306/A120 5 6 |
| -- | 70.0 | °C | ASTM D1525, ISO 306/B120 6 7 |
| Примечание |
|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |