Riblene® FF 29
| Категория | LDPE, Low Density Polyethylene |
| Производитель | Versalis S.p.A. |
| Торговая марка | Riblene® |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
a9gsLl_Riblene-FF-29.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Riblene FF 29 is a high molecular weight low density polyethylene (LDPE), suitable for blown film extrusion.
Riblene FF 29 is characterised by a good melt strength leading to a good bubble stability during extrusion.
Films manufactured by Riblene FF 29 are easily heat shrinkable and characterised by good mechanical properties.
Main Application
Riblene FF 29 is recommended for the production of shrink film for medium loads, for agricultural film and for blend.
Riblene FF 29 is characterised by a good melt strength leading to a good bubble stability during extrusion.
Films manufactured by Riblene FF 29 are easily heat shrinkable and characterised by good mechanical properties.
Main Application
Riblene FF 29 is recommended for the production of shrink film for medium loads, for agricultural film and for blend.
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.921 | g/cm³ | ISO 1183 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.60 | g/10 min | ISO 1133 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Коэффициент трения (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 70 | µm | |
| Толщина пленки-рекомендовано/доступно | 50 to 150 µm | ||
| Модуль растяжения | ISO 527-3 | ||
| 1% Secant, MD : 70 µm, Blown Film | 160 | MPa | |
| 1% Secant, TD : 70 µm, Blown Film | 180 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 70 µm, Blown Film | 10.0 | MPa | |
| TD : Yield, 70 µm, Blown Film | 10.0 | MPa | |
| MD : Break, 70 µm, Blown Film | 26.0 | MPa | |
| TD : Break, 70 µm, Blown Film | 25.0 | MPa | |
| Удлинение при растяжении | ISO 527-3 | ||
| MD : Break, 70 µm, Blown Film | 400 | % | |
| TD : Break, 70 µm, Blown Film | 600 | % | |
| Ударное падение Dart 1(70 µm, Blown Film) | 310 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 70.0 µm | 20.0 | kN/m | |
| TD : 70.0 µm | 30.0 | kN/m |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Температура ломкости | < -75.0 | °C | ASTM D746 |
| Викат Температура размягчения | 91.0 | °C | ISO 306/A |
| Температура плавления | 111 | °C | Internal Method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°, 70.0 µm, Blown Film) | 40 | ASTM D2457 | |
| Haze (70.0 µm, Blown Film) | 18 | % | ISO 14782 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Температура расплава | 180 to 210 | °C |
| Примечание | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Тип материала | Категория | Производитель |
|---|---|---|
| PrimaFlex® LD 19009 | LDPE | Plastic Solutions, Inc. |
| 陶氏低密度聚乙烯 218C | LDPE | The Dow Chemical Company |
| DOW™ LDPE 4016 | LDPE | The Dow Chemical Company |
| NEXUS PE LDPE-0319 | LDPE | Nexus Resin Group, LLC. |
| ECP 125 | LDPE | TBA Electro Conductive Products Ltd. |
| Polene LDPE SU 1018 | LDPE | TPI Polene Public Company Limited |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved