Описание материалов:
OREVAC® T 9304 is a random terpolymer of ethylene, vinyl acetate and maleic anhydride made by high-pressure radicalar polymerization process. As an ethylene copolymer, OREVAC® T 9304 is compatible with PE in all proportions, and with most other ethylene copolymers. Vinyl acetate brings softness, flexibility and polarity, maleic anhydride gives reactivity, leading to versatile adhesive properties to polar and non polar substrates. As a result of high-pressure polymerisation in tubular reactor, OREVAC® T 9304 exhibits high transparency (low haze).
Applications
OREVAC® T 9304 is compatible with most tackifying resins and waxes and can be used for hot melt adhesives formulations. OREVAC® T 9304 is also suitable to produce thermo-adhesive films for solid substrates like PA, PET & PU films, aluminium foils, fiber mats, foams... OREVAC® T 9304 can also be used as a tie layer between polyethylene and polyamide in blown film coextrusion.
| Главная Информация | |
|---|
| Характеристики | - Хорошая адгезия
- Хорошая гибкость
- Высокая четкость
- Мягкий
- Терполимер
|
| Используется | |
| Метод обработки | - Выдувная пленка
- Соэкструдированная пленка
- Экструзионная пленка
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.950 | g/cm³ | ISO 1183, ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 5.5 to 9.3 | g/10 min | ASTM D1238, ISO 1133 |
| Содержание винилацетата | 23.5 to 26.5 | wt% | |
| Maleic Anhydride Content | 1600 | ppm | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ring and Ball Softening Point | 150 | °C | ASTM E28 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore A, 2.80 mm, Compression Molded) | 82 | | ASTM D2240, ISO 868 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение | | | |
| Break, 2.80 mm, Compression Molded 1 | 26.0 | MPa | ASTM D638 |
| Break, 2.80 mm, Compression Molded | 26.0 | MPa | ISO 527-2/5A/50 |
| Удлинение при растяжении | | | |
| Break, 2.80 mm, Compression Molded 2 | 600 to 900 | % | ASTM D638 |
| Break, 2.80 mm, Compression Molded | 600 to 900 | % | ISO 527-2/5A/50 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Викат Температура размягчения | 43.0 | °C | ISO 306/A, ASTM D1525 3 |
| Температура плавления | 80.0 | °C | ISO 11357-3 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | < 230 | °C | |
| Примечание |
|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | Loading 1 (10 N) |