Monprene® IN-22958D (PRELIMINARY DATA)
Описание материалов:
Monprene IN-22958D XRD1 is a high performance thermoplastic elastomer designed specifically for demanding industrial applications including slip coats. Monprene IN-22958D is a high hardness, low density, UV stabilized, unfilled grade with a low coefficient of friction that can be processed by extrusion, co-extrusion and thin extrusion coating.
| Главная Информация | |
|---|
| Характеристики | - Низкий удельный вес
- Без наполнителей
- Низкая плотность
- Высокая гладкость
- Стабилизация света
- Хорошая устойчивость к ультрафиолетовому излучению
- Хорошая адгезия
- Средняя степень жидкости
- Смазка
- Высокая твердость
|
| Используется | - Тонкое покрытие
- Шайба
- Промышленное применение
- Фитинги для труб
- Замена резины
- Профиль
|
| Соответствие RoHS | |
| Внешний вид | |
| Формы | |
| Метод обработки | - Коэкструзионное формование
- Экструзия
- Покрытие
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 0.888 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (230°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра | | | ASTM D2240 |
| Shaw D, 1 sec | 56 | | ASTM D2240 |
| Shaw D, 5 seconds | 53 | | ASTM D2240 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress 1 | | | ASTM D412 |
| Transverse flow
: 100% strain | 10.2 | MPa | ASTM D412 |
| Flow
: 100% strain | 12.8 | MPa | ASTM D412 |
| Transverse flow
: 300% strain | 10.7 | MPa | ASTM D412 |
| Flow
: 300% strain | 13.1 | MPa | ASTM D412 |
| Прочность на растяжение 2 | | | ASTM D412 |
| Transverse flow
: Fracture | 12.2 | MPa | ASTM D412 |
| Flow
: Fracture | 14.8 | MPa | ASTM D412 |
| Удлинение при растяжении 3 | | | ASTM D412 |
| Transverse flow
: Fracture | 350 | % | ASTM D412 |
| Flow
: Fracture | 660 | % | ASTM D412 |
| Tear Strength 4 | | | ASTM D624 |
| Transverse flow | 81.3 | kN/m | ASTM D624 |
| Flow | 153 | kN/m | ASTM D624 |
| Комплект сжатия 5 | | | ASTM D395B |
| 23°C, 22 hr | 26 | % | ASTM D395B |
| 70°C, 22 hr | 57 | % | ASTM D395B |
| Юридическое заявление |
|---|
| The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries. |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Зона цилиндра 1 темп. | 204 - 227 | °C | |
| Зона цилиндра 2 температура. | 204 - 227 | °C | |
| Зона цилиндра 3 темп. | 204 - 227 | °C | |
| Зона цилиндра 4 темп. | 204 - 227 | °C | |
| Зона цилиндра 5 темп. | 204 - 227 | °C | |
| Температура матрицы | 204 - 227 | °C | |
| Инструкции по экструзии |
|---|
| Screw Speed: 30 to 100 rpm;Drying is not necessary. However, if moisture is a problem, dry the pellets for 2 to 4 hours at 150°F (65°C). |
| Примечание |
|---|
| 1 . | C mold, 510mm/min |
| 2 . | C mold, 510mm/min |
| 3 . | C mold, 510mm/min |
| 4 . | C mold, 510mm/min |
| 5 . | Type 1 |