OnForce™ LFT LFT PP-30 LGF/000 1001
Описание материалов:
PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. These products exhibit enhanced physical and mechanical properties versus standard short fiber products. Benefits of LFT compounds include improved impact strength, elastic modulus, and material strength across wide temperature ranges from subambient to highly elevated. Furthermore, LFT compounds have been shown to offer improved performance in the areas of creep and fatigue performance, improved dimensional stability, and exhibit an exceptional surface finish when compared to traditional highly filled short fiber products.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Длинное стекловолокно, 30% наполнитель по весу
|
| Соответствие RoHS | |
| Формы | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.12 | g/cm³ | ASTM D792 |
| Формовочная усадка-
Поток | 0.20 to 0.30 | % | ASTM D955 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 6300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 110 | MPa | ISO 527-2 |
| Растяжимое напряжение (Break) | 3.0 | % | ISO 527-2 |
| Флекторный модуль | 6100 | MPa | ISO 178 |
| Флекторный стресс | 145 | MPa | ISO 178 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод ударная прочность (23°C) | 22 | kJ/m² | ISO 180 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 145 | °C | ISO 75-2/A |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 85.0 | °C | |
| Время сушки | 2.0 | hr | |
| Температура обработки (расплава) | 210 to 221 | °C | |
| Температура формы | 65.6 | °C | |