TOTAL Polyethylene Lumicene® M 2710 EP (EU)
Описание материалов:
Lumicene® mPE M 2710 EP is a second generation metallocene based Low Density Polyethylene with hexene as comonomer.
Lumicene® mPE M 2710 EP can be processed at high output rates with low extrusion pressure, excellent bubble stability and gauge control in comparison with conventional LLDPE and first generation metallocene based polyethylene. The combination of these features brings a significant downgauging potential.
Lumicene® mPE M 2710 EP is especially dedicated to film applications where high gloss and high transparency are required, particularly in blend and in coextrusion with LLDPE or LDPE.
Lumicene® mPE M 2710 EP is suited for many applications in the field of consumer, industrial, food or hygiene packaging such as bags, deep freeze, collation shrink and lamination.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Хорошее тепловое уплотнение
- Хорошая жесткость
- Хорошая прочность на разрыв
- Термогерметичный
- Гексен-комномер
- Высокая четкость
- Глянцевый
- Стойкий к проколу
|
| Используется | - Сумки
- Смешивание
- Потребительские приложения
- Пленка
- Пищевая упаковка
- Промышленное применение
- Ламинаты
- Многослойная пленка
- Упаковка
- Термоусадочная пленка
|
| Рейтинг агентства | |
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 0.927 | g/cm³ | ASTM D792, ISO 1183 |
| Массовый расход расплава (MFR) | | | |
| 190°C/2.16 kg | 0.90 | g/10 min | ASTM D1238, ISO 1133 |
| 190°C/21.6 kg | 30 | g/10 min | ASTM D1238 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Коэффициент трения (vs. Itself - Static, Blown Film) | 0.50 | | ASTM D1894 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Сектантный модуль | | | ASTM D882A |
| 1% Secant, MD
: 25 µm, Blown Film | 214 | MPa | |
| 1% Secant, TD
: 25 µm, Blown Film | 172 | MPa | |
| Tensile Stress | | | |
| MD
: Yield, 40 µm, Blown Film | 13.5 | MPa | ISO 527-3 |
| TD
: Yield, 40 µm, Blown Film | 14.0 | MPa | ISO 527-3 |
| MD
: Break, 25 µm, Blown Film | 33.8 | MPa | ASTM D882A |
| TD
: Break, 25 µm, Blown Film | 33.1 | MPa | ASTM D882A |
| MD
: Break, 40 µm, Blown Film | 51.0 | MPa | ISO 527-3 |
| TD
: Break, 40 µm, Blown Film | 48.0 | MPa | ISO 527-3 |
| Удлинение при растяжении | | | |
| MD
: Break, 25 µm, Blown Film | 580 | % | ASTM D882A |
| TD
: Break, 25 µm, Blown Film | 720 | % | ASTM D882A |
| MD
: Break, 40 µm, Blown Film | 650 | % | ISO 527-3 |
| TD
: Break, 40 µm, Blown Film | 720 | % | ISO 527-3 |
| Ударное падение Dart | | | |
| 25 µm, Blown Film | 150 | g | ASTM D1709A |
| 40 µm, Blown Film | 200 | g | ISO 7765-1 |
| Elmendorf Tear Strength -
TD (25 µm, Blown Film) | 500 | g | ASTM D1922 |
| Температура инициализации уплотнения (25 µm, Blown Film) | 112 | °C | |
| Передача водяного пара | 14 | g/m²/24 hr | ASTM E96 |
| Elmendorf Tear Strength 1 | | | ISO 6383-2 |
| MD
: 40.0 µm | 60.0 | kN/m | |
| TD
: 40.0 µm | 160.0 | kN/m | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Викат Температура размягчения | 118 | °C | ISO 306 |
| Температура плавления | | | |
| -- | 119 | °C | ISO 11357-3 |
| -- | 121 | °C | ASTM D3417 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блестящий Гарднер (45°, 25.4 µm, Blown Film) | 65 | | ASTM D523 |
| Блеск (45°, 40.0 µm, Blown Film) | 70 | | ASTM D2457 |
| Haze | | | |
| 25.4 µm, Blown Film | 7.0 | % | ASTM D1003 |
| 40.0 µm, Blown Film | 6.5 | % | ISO 14782 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | 193 to 210 | °C | |