- Synthos EPS® 0816F/PL
Synthos EPS® 0816F/PL
| Категория | PS, Expanded Polystyrene , PS (EPS) |
| Производитель | Synthos S.A. |
| Торговая марка | Synthos EPS® |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
XHC2N5_Synthos-EPS-0816F-PL.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Synthos EPS® F /PL type 0308F, 0513F, 0816F and 1325F is self-extinguishing expandable polystyrene EPS with high content of pentane. The materials are formed by spherical polystyrene particles that contain a flame retardant system (content of HBCD < 0,5%) and a hydrocarbon blowing agent. Their surface is treated against gluing during processing and the formation of electrostatic charge. Due to the content of halogenated flame retardant and the residual blowing agent, the product is unsuitable for objects intended for direct contact with food.
Synthos EPS® 0816F/PL (Owipian FS 0816) is mainly used for production of blocks with medium and higher density; of cutted boards and profiles from the blocks for a thermal insulation e.g. building objects or in packaging technology.
Synthos EPS® 0816F/PL (Owipian FS 0816) is mainly used for production of blocks with medium and higher density; of cutted boards and profiles from the blocks for a thermal insulation e.g. building objects or in packaging technology.
| Главная Информация | |
|---|---|
| Добавка |
|
| Характеристики |
|
| Используется |
|
| Внешний вид |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Видимая плотность | Internal Method | ||
| -- 1 | < 0.02 | g/cm³ | |
| -- 2 | 0.02 to 0.04 | g/cm³ | |
| Moisture Content | < 7000 | ppm | Internal Method |
| Размер частиц- > 95% между | 0.800 to 1.60 | mm | Internal Method |
| Воспламеняемость | Номинальное значение | Метод испытания | |
|---|---|---|---|
| Реакция на огонь | |||
| -- | B1 | DIN 4102 | |
| -- | Class E | EN 13501-1 |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Дующий агент | < 7.0 | wt% | Internal Method |
| Примечание | |
|---|---|
| 1 . | The laboratory tests of expanded beads bulk density are made according to Polish Standard PN-90/C-89298 using the following expansion times: 0308 and 0513: 12 min., 0816: 10 min., 1325: 6 min. |
| 2 . | The typical bulk density indicates values obtained during single-step pre-foaming on continuous pre-foaming devicesLower values of bulk density can be achieved only after multiple pre-expansion. |
| Тип материала | Категория | Производитель |
|---|---|---|
| MARPOL® F-M | PS (EPS) | Marco Polo International, Inc. |
| Expandable PS F42MB | PS (EPS) | INEOS Styrenics International SA |
| Eporex® 550 | PS (GPPS) | Eternal Plastics Co., Ltd. |
| Latilub 30/R-07 GRT | PS (GPPS) | LATI S.p.A. |
| Osterlene® CIE-9-00 | PS (GPPS) | Osterman & Company |
| EPS Silver® S400LR | PS (EPS) | INEOS Styrenics International SA |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved