Escor™ 5050

Категория	EAA, Ethylene Acrylic Acid Copolymer Resin
Производитель	ExxonMobil Chemical
Торговая марка	Escor™
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	XGiG6O_Escor-5050.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

Escor 5000 is mainly used for extrusion coating, coextrusion coating and extrusion compounding. It can be well bonded to polar substrates, aluminum foils, metal films, paper, steel and glass surfaces. Provides an excellent balance of adhesion to the surface of the substrate and interlayer adhesion to coextruded low density polyethylene and ethylene vinyl acetate. Excellent adhesive polymer in film.

Главная Информация

Физический	Номинальное значение	Единица измерения	Метод испытания
Массовый расход расплава (MFR) (190°C/2.16 kg)	8.4	g/10 min	ASTM D1238
Содержание акриловой кислоты	9.0	wt%	ExxonMobil Method

Юридическое заявление
本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用有关潜在食品接触应用合规信息（例如：FDA、EU、HPFB），请与埃克森美孚化工客户服务代表联系。

Инструкции по экструзии
Excellent results are obtained in extrusion coating at 260°C - 280°C (500°F - 536°F) temperature range. Processing temperatures above 300°C (572°F) may cause resin degradation. To minimize corrosion risk, all exposed metal surfaces in the extruder and die should be made from corrosion resistant metals or nickel/chrome plated. ESCOR should be fed into the extruder after LDPE of a similar or higher melt index. Machines should always be completely purged with LDPE or a suitable cleaning compound before shutdown.

Инструкции по экструзии

Excellent results are obtained in extrusion coating at 260°C - 280°C (500°F - 536°F) temperature range. Processing temperatures above 300°C (572°F) may cause resin degradation. To minimize corrosion risk, all exposed metal surfaces in the extruder and die should be made from corrosion resistant metals or nickel/chrome plated. ESCOR should be fed into the extruder after LDPE of a similar or higher melt index. Machines should always be completely purged with LDPE or a suitable cleaning compound before shutdown.

Тип материала	Категория	Производитель
Nucrel® 3990	EAA	DuPont Packaging & Industrial Polymers
Escor™ 5000	EAA	ExxonMobil Chemical
Lotader® HX8290	EAA	Arkema
PRIMACOR™ 1410	EAA	The Dow Chemical Company
Nucrel® 30907	EAA	DuPont Packaging & Industrial Polymers
Bynel® 21E533	EAA	DuPont Packaging & Industrial Polymers

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

