LUVOCOM® 80-7919 VP

Категория	POM, Acetal (POM) Copolymer
Производитель	Lehmann & Voss & Co.
Торговая марка	LUVOCOM®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	WgxW2T_LUVOCOM-80-7919-VP.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOCOM®80-7919 VP is a polyoxymethylene (POM) copolymer material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 80-7919 VP are:

Wear-resistant

Lubrication

Typical application areas include:

engineering/industrial accessories

textile/fiber

Automotive Industry

business/office supplies

Главная Информация
Добавка	Ptfe лубрикант
Характеристики	Низкий коэффициент трения Хорошая мобильность Хорошая стойкость к истиранию Смазка
Используется	Шестерня Текстильные изделия Инженерные аксессуары Применение в автомобильной области Бизнес-оборудование Камера Подшипник
Внешний вид	Натуральный цвет

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.49	g/cm³	ISO 1183
Плавкий объем-расход (MVR) (190°C/2.16 kg)	33.0	cm³/10min	ISO 1133
Формовочная усадка	1.8 - 2.6	%	DIN 16901
Поглощение воды (23°C, 24 hr)	0.15	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	2200	MPa	ISO 527-2
Tensile Stress (Break)	45.0	MPa	ISO 527-2
Растяжимое напряжение (Yield)	7.5	%	ISO 527-2
Флекторный модуль	1800	MPa	ISO 178
Флекторный стресс	65.0	MPa	ISO 178
Коэффициент трения
Dynamic	0.16
Static	0.080
Flexural Strain at Flexural Strength	10	%	ISO 178

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Максимальная рабочая температура- Короткий срок	120	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Ударная прочность			ISO 179/1eA
-30°C	2.5	kJ/m²	ISO 179/1eA
23°C	3.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength
-30°C	34	kJ/m²	ISO 179/1fU
23°C	36	kJ/m²	ISO 179/1eU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Температура непрерывного использования	100	°C	UL 746B
Викат Температура размягчения	145	°C	ISO 306/A

Инъекция	Номинальное значение	Единица измерения
Температура сушки
A	75.0	°C
Dehumidification desiccant, B	120	°C
Время сушки
A	2.0 - 8.0	hr
Dehumidification desiccant, B	2.0 - 4.0	hr
Задняя температура	175 - 190	°C
Средняя температура	185 - 205	°C
Передняя температура	180 - 200	°C
Температура сопла	175 - 200	°C
Температура обработки (расплава)	200	°C
Температура формы	80.0 - 120	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information If originally sealed containers are used, it is normally possible to omit the predrying stage. If PTFE materials are not predried, an increase in deposits inside the mould may occur. When changing from higher melting-point polymers such as polyamides to this product, extremely thorough intermediate cleaning should be carried out. Processing temperatures above 215°C may very rapidly cause thermal damage and should therefore be avoided, particularly as formaldehyde may be eliminated here. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information If originally sealed containers are used, it is normally possible to omit the predrying stage. If PTFE materials are not predried, an increase in deposits inside the mould may occur. When changing from higher melting-point polymers such as polyamides to this product, extremely thorough intermediate cleaning should be carried out. Processing temperatures above 215°C may very rapidly cause thermal damage and should therefore be avoided, particularly as formaldehyde may be eliminated here. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Тип материала	Категория	Производитель
Sindustris POM FW701N	Acetal (POM) Homopolymer	Sincerity Australia Pty Ltd.
Tarnoform® 411	Acetal (POM) Copolymer	Grupa Azoty S.A.
DynaStat® 1847	Acetal (POM) Copolymer	Polymer Dynamix
KOCETAL® WR301LOBK	Acetal (POM) Copolymer	Kolon Plastics, Inc.
LTP ZW-3212	Acetal (POM) Copolymer	Chengdu Letian Plastics Co., Ltd
Tarnoform® 300 GF2	Acetal (POM) Copolymer	Grupa Azoty S.A.

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

