Описание материалов:
Menzolit® SMC 0400 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is a must to work with chrome plated tools. The product contains no halogens or heavy metals.
Menzolit® SMC 0400 is a Class-A SMC for exterior body applications on cars, LCV´s and trucks. These compounds mould to parts with good up to excellent surface quality for medium bake in-line and off-line painted (100 - 140°C) body panels. Surface defects like waviness, fibre patterns and orange peel do not occur with this products. To achieve the highest surface quality, we recommend that tool surfaces are mirror polished. To ease demoulding we highly recommend chrome-plating of tool surfaces. Menzolit® SMC 0400 allows. The product shows very good adhesion to paint or In Mould Coating (IMC). Because of its zero shrink properties warpage is eliminated and parts reproducing the dimensions of the cold mould can be produced.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Стекло \ Mineral, 30% наполнитель по весу
|
| Характеристики | - Огнестойкий
- Хорошая адгезия
- Хорошая поверхность
- Без галогенов
- Высокая термостойкость
- Низкая усадка
- Низкий уровень дыма
- Низкий уровень защиты
|
| Используется | - Автомобильные Приложения
- Автомобильные внешние части
|
| Внешний вид | |
| Формы | - Smc-лист формовочный состав
|
| Метод обработки | |
| Код маркировки деталей (ISO 11469) | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 1.90 | g/cm³ | ISO 1183 |
| Формовочная усадка | | | |
| -- 1 | 0.0 | % | DIN 53464 |
| -- | -0.050 | % | ISO 2577 |
| Поглощение воды (Saturation, 23°C) | < 0.50 | % | ISO 62 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения (Compression Molded) | 11000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 90.0 | MPa | ISO 527-2 |
| Растяжимое напряжение (Break, Compression Molded) | 1.5 | % | ISO 527-2 |
| Флекторный модуль (Compression Molded) | 10000 | MPa | ISO 178 |
| Флекторный стресс (Compression Molded) | 180 | MPa | ISO 178 |
| Сжимающее напряжение | 100 | MPa | ISO 14126 |
| Poisson's Ratio | 0.30 | | Internal Method |
| Matrix Crazing Strain | 0.40 | % | Internal Method |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность (Compression Molded) | 80 | kJ/m² | ISO 179 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | °C | ISO 75-2/A |
| Температура непрерывного использования | 165 | °C | ISO 14126 |
| Температура перехода стекла | 200 | °C | DSC |
| CLTE-
Поток | 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Воспламеняемость | Номинальное значение | | Метод испытания |
|---|
| Огнестойкость (3.00 mm) | HB | | UL 94 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 140 to 160 | °C | |
| Давление впрыска | 8.00 to 10.0 | MPa | |
| Примечание |
|---|
| 1 . | Post Molding Shrinkage |