DOW™ HDPE DGDC-2100 NT 7
| Категория | HDPE, High Density Polyethylene Resin |
| Производитель | The Dow Chemical Company |
| Торговая марка | DOW™ HDPE |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
W7Hss2_DOW-HDPE-DGDC-2100-NT-7.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
- High Density Polyethylene (HDPE)
- Complies with:
- U.S. FDA 21 CFR 177.1520 (c) 3.2a
- Canadian HPFB No Objection
- EU, No 10/2011
- Consult the regulations for complete details.
DOW DGDC-2100 NT 7 High Density Polyethylene Resin is a high-molecular weight, high-density film grade resin. This product was specifically designed to offer an optimal balance of physical properties and processability. DGDC-2100 NT7 HDPE resin is ideally suited for use in making grocery sacks, consumer and institutional liners, and merchandise bags.
| Главная Информация | |
|---|---|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.948 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.070 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 9.0 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 13 | µm | |
| Энергия прокола пленки (13 µm) | 0.893 | J | Internal method |
| Сила прокола пленки (13 µm) | 29.8 | N | Internal method |
| Сопротивление проколу пленки (13 µm) | 10.6 | J/cm³ | Internal method |
| Сектантный модуль | ASTM D882 | ||
| 2% secant, MD : 13 µm | 966 | MPa | ASTM D882 |
| 2% secant, TD : 13 µm | 1100 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield, 13 µm | 42.4 | MPa | ASTM D882 |
| TD : Yield, 13 µm | 31.8 | MPa | ASTM D882 |
| MD : Broken, 13 µm | 93.4 | MPa | ASTM D882 |
| TD : Broken, 13 µm | 68.8 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Broken, 13 µm | 330 | % | ASTM D882 |
| TD : Broken, 13 µm | 410 | % | ASTM D882 |
| Ударное падение Dart (13 µm) | 350 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 13 µm | 11 | g | ASTM D1922 |
| TD : 13 µm | 73 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Температура плавления (DSC) | 128 | °C | Internal method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°, 12.7 µm) | 9 | ASTM D2457 | |
| Haze (12.7 µm) | 69 | % | ASTM D1003 |
| Инструкции по экструзии |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：1.97 英寸 (50mm)；24:1 L/D 熔体温度：410 °F (210 °C) 输出：模具周长的 8 磅/小时/英寸 模具直径：3.94 英寸 (100mm) 放大比：4:1 内缩高度：32 英寸 (813 mm) |
| Тип материала | Категория | Производитель |
|---|---|---|
| TABOREX TA 1132 HD | HDPE | SILON s.ro |
| ALKATEQ™ HD3690P | HDPE | Marplex Australia Pty. Ltd. |
| Eltex® A4009MFN1325 | HDPE | INEOS Olefins & Polymers Europe |
| MARPOL® HDM 507 | HDPE | Marco Polo International, Inc. |
| Qenos PE GE4760 | HDPE, MMW | Qenos Pty Ltd |
| Marlex® HXB TR-494 | HDPE, UHMW | Chevron Phillips Chemical Company LLC |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved