Sarlink® TPV X4145B-W1 BLACK (PRELIMINARY DATA)
Описание материалов:
SARLINK® X4145BW1 BLACK is a specially developed engineering material designed primarily for demanding consumer, industrial, and automotive applications. SARLINK® X4145BW1 BLACK is a low density, medium hardness thermoplastic vulcanizate that exhibits excellent compression set, flex fatigue, high and low temperature performance and very good chemical resistance including copper contact. This grade can be processed by injection molding, extrusion, and profile extrusion.
| Главная Информация | |
|---|
| Характеристики | - Низкий удельный вес
- Низкая деформация сжатия
- Низкая плотность
- Обрабатываемость, хорошая
- Хорошая прочность расплава
- Хорошая химическая стойкость
- Теплостойкость, высокая
- Заполнение
- Стабильность контакта меди
- Гибкий
- Средняя твердость
|
| Используется | - Уплотнительные кольца
- Штепсельная Вилка
- Втулка
- Большая бытовая техника и мелкая бытовая техника
- Шайба
- Диафрагма
- Промышленное применение
- Детали бытовой техники
- Уплотнение
- Применение в автомобильной области
- Замена резины
- Применение потребительских товаров
- Профиль
|
| Соответствие RoHS | |
| Внешний вид | |
| Формы | |
| Метод обработки | - Экструзия
- Экструзионное формование профиля
- Литье под давлением
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.960 | g/cm³ | ISO 1183 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра | | | ISO 868 |
| Shaw A, 5 seconds, extruded | 45 | | ISO 868 |
| Shore A, 5 seconds, injection molding | 48 | | ISO 868 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Растяжимое напряжение-
Поперечный поток (100% Strain) | 1.40 | MPa | ISO 37 |
| Растяжимое напряжение-
Поперечный поток (Break) | 4.10 | MPa | ISO 37 |
| Растяжимое удлинение-
Поперечный поток (Break) | 500 | % | ISO 37 |
| Прочность на разрыв-
Поперечный поток 1 | 20 | kN/m | ISO 34-1 |
| Комплект сжатия | | | ISO 815 |
| 23°C, 22 hr | 14 | % | ISO 815 |
| 70°C, 22 hr | 27 | % | ISO 815 |
| Анализ заполнения | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Видимая вязкость (200°C, 206 sec^-1) | 323 | Pa·s | ASTM D3835 |
| Юридическое заявление |
|---|
| The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries. |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 82 | °C | |
| Время сушки | 3.0 | hr | |
| Задняя температура | 177 - 216 | °C | |
| Средняя температура | 177 - 216 | °C | |
| Передняя температура | 177 - 216 | °C | |
| Температура сопла | 188 - 221 | °C | |
| Температура обработки (расплава) | 182 - 221 | °C | |
| Температура формы | 10 - 66 | °C | |
| Back Pressure | 0.0689 - 1.03 | MPa | |
| Screw Speed | 100 - 200 | rpm | |
| Отношение винта L/D | 20.0:1.0 | | |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 82 | °C | |
| Время сушки | 3.0 | hr | |
| Зона цилиндра 1 темп. | 182 - 204 | °C | |
| Зона цилиндра 2 температура. | 182 - 204 | °C | |
| Зона цилиндра 3 темп. | 188 - 210 | °C | |
| Зона цилиндра 4 темп. | 188 - 210 | °C | |
| Температура расплава | 193 - 216 | °C | |
| Температура матрицы | 193 - 216 | °C | |
| Рулон для снятия | 21 - 49 | °C | |
| Инструкции по экструзии |
|---|
| Screen Pack: 20 to 60 meshScrew: 3:1 Compression Ratio |
| Примечание |
|---|
| 1 . | Method B, right-angle specimen (without cut) |