HIPLEX® TR-130, copolymer of ethylene and hexene is tailored for blown film production. Extraordinary melt toughness made possible to get film down to 0.006 mm thickness. Extruded film has high impact resistance, good tear strength, excellent antiblock and good barrier properties, low gel content and excellent sealing and printing properties.
Applications:
HIPLEX® TR-130 is suitable for production of advertising bags, industrial bags, bags for food package, and for production of composite films and blends with other kind of polyethylene.
HIPLEX® TR-130 has Health Certificate issued by Institute for Health Protection of Serbia. Also, HIPLEX® TR-130 has Statement of Conformity, which declares product's conformity with the European norms for materials intended to come into contact with foodstuffs. Statement of Conformity is issued by Institute for Public Health, Maribor, Slovenia.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Антиблокировка
- Барьерная смола
- Сополимер
- Отличная Печатающая способность
- Приемлемый пищевой контакт
- Хорошее тепловое уплотнение
- Хорошая прочность расплава
- Хорошая прочность на разрыв
- Гексен-комномер
- Высокая ударопрочность
- Низкий гель
|
| Используется | - Сумки
- Смешивание
- Пленка
- Пищевая упаковка
|
| Рейтинг агентства | |
| Формы | |
| Метод обработки | - Выдувная пленка
- Экструзионная пленка
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.940 | g/cm³ | ISO 1183 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.18 | g/10 min | ISO 1133 |
| Экологическое сопротивление растрескиванию (F50) | > 1000 | hr | ASTM D1693B |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость по суше (Shore D) | 58 | | ISO 868 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ISO 527-2 |
| Yield | 18.0 | MPa | |
| Break | 32.0 | MPa | |
| Растяжимое напряжение (Break) | 900 | % | ISO 527-2 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 25 | µm | |
| Tensile Stress | | | ISO 527-3 |
| MD
: Yield, 25 µm | 24.0 | MPa | |
| TD
: Yield, 25 µm | 19.0 | MPa | |
| MD
: Break, 25 µm | 43.0 | MPa | |
| TD
: Break, 25 µm | 33.0 | MPa | |
| Удлинение при растяжении | | | ISO 527-3 |
| MD
: Break, 25 µm | 550 | % | |
| TD
: Break, 25 µm | 700 | % | |
| Ударное падение Dart (25 µm) | 88 | g | ASTM D1709 |
| Elmendorf Tear Strength 1 | | | ASTM D1922 |
| MD
: 25.0 µm | 42.5 | kN/m | |
| TD
: 25.0 µm | 251.0 | kN/m | |
| Дополнительная информация | Номинальное значение | Единица измерения | |
|---|
| Температура выдувного формования 2 | 195 to 220 | °C | |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | No Break | | ISO 180 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Викат Температура размягчения | 120 | °C | ISO 306 |
| Примечание |
|---|
| 1 . | Blown Film |
| 2 . | Blow-up ratio: 3.5-5 : 1, Neck height: 6-10 times die diameter |