Описание материалов:
Plexar tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins and copolymers, EVA, EMA, polypropylene, polyamide (nylon), ethylene vinyl alcohol copolymers (EVOH), ionomer and other sealants, polyethylene terephthalate (PET) resins and copolymers, styrenic polymers, metal, and paperboard. Product grades primarily used for blown and cast films, sheet and thermoforming, blow molding, extrusion coating and lamination, tubing, pipe, and other specialty applications are available in pellet form. Contact your Plexar sales and/or Equistar technical service representative for more information and specific recommendations for your application(s).
| Главная Информация | |
|---|
| Используется | - Клеи
- Пищевая упаковка
- Промышленное применение
- Упаковка
|
| Рейтинг агентства | - Управление по санитарному надзору за качеством пищевых продуктов и медикаментов 21 CFR 175,105
|
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.943 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение (Break) | 17.2 | MPa | ASTM D638 |
| Удлинение при растяжении (Break) | 25 | % | ASTM D638 |
| Флекторный модуль-
1% Secant | 545 | MPa | ASTM D790 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Викат Температура размягчения | 112 | °C | ASTM D1525 |
| Время индукции окисления | > 20 | min | ASTM D3985 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | > 210 | °C | |