Описание материалов:
Geon® 186A is low molecular weight homopolymer resin, providing a good balance of fused film physical properties and fusion characteristics. It provides excellent chemical foam characteristics with good overblow resistance. It gives good dispersability for plastisol preparation.
Geon® 186A is recommended for applications where an overall balance of good rheological and fused film physical properties are required such as low density chemcially blown foams, fabric coating applications, and plastisol screen printing inks.
| Главная Информация | |
|---|
| Характеристики | - Foamable свойство
- Средний Молекулярный вес
|
| Используется | |
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.40 | g/cm³ | ASTM D792 |
| K-Value 1 | 65.0 | | Internal method |
| Внутренняя вязкость | 1.0 | | ASTM D1243-60-A |
| Влажность-
Карл Фишер 2 | 0.060 | % | Internal method |
| Плотность объема | 400 | g/l | |
| Relative Viscosity 3 | 2.20 | | Internal method |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Оптимальное растяжение-
ПП 4 | 20.7 | MPa | ASTM D638 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блеск-
60 градусов плавленый 5 минут @ 350F 5 | 87 | % | Internal method |
| Прозрачность-коэффициент пропускания-
ПП 6 | 78 | % | Internal method |
| Анализ заполнения | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Вязкость брокфилда | | | Internal method |
| Initial Viscosity @ 2 rpm 7 | 9.00 | Pa·s | Internal method |
| Initial Viscosity @ 20 rpm 8 | 6.95 | Pa·s | Internal method |
| One Day Viscosity @ 2 rpm 9 | 12.6 | Pa·s | Internal method |
| One Day Viscosity @ 20 rpm 10 | 9.28 | Pa·s | Internal method |
| Отрежьте отток-
95 фунтов на квадратный дюйм 11 | 90.00 | g/10 min | Internal method |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Северная тонкость 12 | 4.75 | Hegman | Internal method |
| Остаточный винилхлорид мономер 13 | | ppm | Internal method |
| Добываемый метанол 14 | 3.5 | % | Internal method |
| Процесс полимеризации | Dispersion | | |
| Температура геля-
ПП 15 | 72 | °C | Internal method |
| Note:The value set forth represent "typical" values and Mexichem Specialty Resins, therefore, makes no representation that the material in any particular shipment will conform to the listed properties.Packaging: This resin is shipped in multi-wall paper bags, net weight 50 lbs, 2500 lbs per pallet. Information shown on the package includes commercial identification number, lot and weight.Geon® ALTC and ASTM D638 (formulation): 100phr Geon® 186A, 57phr DINP, 3phr ESO, and 2phr Therm-Chek SP 120 LOHFGeon® STP 390 (formulation): 100phr Geon® 186A, and 60phr DOP |
| Примечание |
|---|
| 1 . | Interrelationship |
| 2 . | Karl Fisher-Geon® 683c |
| 3 . | Interrelationship |
| 4 . | With provided formulation |
| 5 . | 60°，FF，ALTC-65 |
| 6 . | Geon® ALTC 66 (with provided formulation) |
| 7 . | Initial, V12,Geon®1010 |
| 8 . | One day, V12,Geon®1010 |
| 9 . | Geon® ALTC 22 (with provided formulation) |
| 10 . | Geon® ALTC 22 (with provided formulation) |
| 11 . | 95 psi，Geon® 1010 |
| 12 . | Geon® 390 |
| 13 . | Geon® STP 1005 |
| 14 . | Geon® 894 |
| 15 . | Geon® ALTC 29 (with provided formulation) |