Описание материалов:
This grade has been developed as a new member of the SABIC® PP FLOWPACT range dedicated to the thin wall packaging market. It is nucleated and is characterized by a high crystallization temperature and excellent flow behaviour in combination with a stiffness to impact balance. This grade was designed for high-speed injection moulding and it enables very cost efficient processing on the basis of easy mould filling and very short cycle times. It has a very good antistatic performance and permits easy demoulding.
This material is typically used in thin wall packing applications both for food and non-food segments. This includes yellow fats/margarine tubs, dairy packaging and housewares. The grade has an excellent dimensional stability what is crucial for the thin wall packaging market.
The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications.
| Главная Информация | |
|---|
| Добавка | - Антистатический
- Нуклеативный агент
|
| Характеристики | - Антистатический
- Блок сополимер
- Цикл быстрого формования
- Хорошая стабильность размеров
- Хороший поток
- Хорошая ударопрочность
- Хороший выпуск пресс-формы
- Хорошая жесткость
- Ядро
|
| Используется | - Контейнеры
- Пищевая упаковка
- Товары для дома
- Упаковка
- Тонкостенная упаковка
|
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Массовый расход расплава (MFR) (230°C/2.16 kg) | 100 | g/10 min | ASTM D1238, ISO 1133 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale) | 95 | | ASTM D785 |
| Твердость по суше (Shore D) | 62 | | ISO 868 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | | | |
| 1% Secant 1 | 1500 | MPa | ASTM D638 |
| -- | 1450 | MPa | ISO 527-2/1A/1 |
| Прочность на растяжение | | | |
| Yield 2 | 24.0 | MPa | ASTM D638 |
| Yield | 25.0 | MPa | ISO 527-2/1A/50 |
| Удлинение при растяжении | | | |
| Yield 3 | 4.0 | % | ASTM D638 |
| Yield | 4.0 | % | ISO 527-2/1A/50 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность | | | ISO 179/1eA |
| 0°C | 6.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Зубчатый изод Impact | | | |
| 0°C | 45 | J/m | ASTM D256A |
| 23°C | 60 | J/m | ASTM D256A |
| 0°C | 5.0 | kJ/m² | ISO 180/1A |
| 23°C | 7.0 | kJ/m² | ISO 180/1A |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | |
| 0.45 MPa, Unannealed | 100 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 95.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 60.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 55.0 | °C | ISO 75-2/Af |
| Викат Температура размягчения | | | |
| -- | 150 | °C | ASTM D1525, ISO 306/A120 5 6 |
| -- | 76.0 | °C | ASTM D1525, ISO 306/B120 6 7 |
| Примечание |
|---|
| 1 . | 5.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |