Bayfill® 382 (47.6:100)

Категория PUR, Polyurethane (MDI) , PUR-MDI
Производитель Covestro - PUR
Торговая марка Bayfill®
Порт Китай Шанхайский порт
Торговые условия FOB, CFR, CIF
Платежное средство L/C, T/T, Western Union
PDF Tbvpwp_Bayfill-382-47-6-100-.pdf
Контактная информация
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Описание материалов:
Bayfill 382 is a semi-rigid polyurethane foam system designed for automotive interior applications. The Bayfill 382 system is an excellent choice for the production of soft-touch panels, such as instrument panels, door trim, and center consoles. The foam is typically molded in a back-filling process between a soft, exterior skin and a rigid, thermoplastic substrate.

The Bayfill 382 system is supplied as two components. Component A is a polymeric diphenylmethane diisocyanate (PMDI). Component B is a polyol mixture. As with any product, use of the Bayfill 382 system in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.
Главная Информация
Используется
  • Пена
  • Применение в автомобильной области
  • Автомобильные внутренние детали
  • Оборудование для салона автомобиля
  • Приборная панель автомобиля
ФизическийНоминальное значениеЕдиница измеренияМетод испытания
Литая плотность 144kg/m³ASTM D3574A
ЭластомерыНоминальное значениеЕдиница измеренияМетод испытания
Отклонение силы сжатия ASTM D3574C
    -- 10.179MPaASTM D3574C
    -- 20.117MPaASTM D3574C
Комплект сжатия ASTM D3574D
    Cd 336%ASTM D3574D
    Cd 429%ASTM D3574D
    Ct 514%ASTM D3574D
    Ct 618%ASTM D3574D
МеханическиеНоминальное значениеЕдиница измеренияМетод испытания
Прочность на растяжение
    -- 70.124MPaASTM D3574K
    -- 0.324MPaASTM D3574E
Удлинение при растяжении
    Fracture 817%ASTM D3574K
    Fracture 44%ASTM D3574E
ЭластомерыНоминальное значениеЕдиница измеренияМетод испытания
Tear Strength 0.175kN/mASTM D3574F
ТермокомплектНоминальное значение
Компоненты термокомплекта
    Component a Mixing ratio by weight: 53
    Component B Mixing ratio by weight: 100
Дополнительная информация
Part A Type: Isocyanate Appearance: Dark brown to black liquid Specific Gravity @ 25°C: 1.24 Viscosity @25°C: 200 cps Flash Point PMCC: 199°C NCO: 31 wt% Part B Type: Polyol Appearance: Black liquid Specific Gravity @ 25°C: 1.01 Viscosity @25°C: 1400 cps Flash Point PMCC: 131°C Water: 2.8 wt% Hydroxyl Number: 70 KOH/g Material Temperatures: 27 to 32°CMold Temperature: 38 to 43°CDemold Time: >90 secHand Mix Reactivity at 25°C Cream Time: 14 to 22 sec Top of Cup Time: 50 to 64 sec Gel Time: 60 to 76 sec Rise Time: 87 to 107 sec Free-Rise Density: 2.9 to 4.5 lb/ft³ Machine Reactivity at 29°C Cream Time: 8 to 12 sec Top of Cup Time: 24 to 30 sec Gel Time: 40 to 45 sec Rise Time: 60 to 65 sec Free-Rise Density: 3.10 to 4.10 lb/ft³ Molded Density: 8.0 to 11.0 lb/ft³
Примечание
1 .0.5
2 .After J2 Autoclave
3 .After J2 Autoclave, Cd=compression set as a percentage of the original deflection
4 .50, Cd=compression set as a percentage of the original deflection
5 .50%, Ct=compression set as a percentage of the original thickness
6 .After J2 Autoclave, Ct=compression set as a percentage of the original thickness
7 .Dry Heat Aged at 140°C
8 .Dry Heat Aged at 140°C
Тип материала Категория Производитель
ADEKA YG-108 PUR-Ester Adeka Corporation
Task® 13 PUR, Unspecified Smooth-On, Inc
Ebalta GM 972 / Comp. A+B PUR, Unspecified Ebalta Kunststoff GmbH
Ebalta SG 241 / Comp. A+B PUR, Unspecified Ebalta Kunststoff GmbH
Andur M-11 (97% HQEE/ 3% TMP) PUR-Ester/MDI Anderson Development Company
Huafon JF-W-3020 PUR, Unspecified Huafon Group Co., Ltd.
Получите информацию об этом продукте следующим способом.
Телефон+086 13424755533
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат

Copyright © russianpolymer.com All Rights Reserved
Получите информацию об этом продукте следующим способом.

Служба поддержки клиентов Вичат
Свяжитесь с нами