Описание материалов:
GI-1220 is a high tear strength, tin-catalyzed RTV-2 silicone rubber, which was designed for casting polyester parts. GI-1220 is especially good for molds with deep undercuts and for molds that require flexing for part removal. GI-1220 is not sensitive to inhibition, meaning it will cure at room temperature over virtually any surface. It is easy to mix and de-air, and will cure with only a slight degree of shrinkage. The speed at which the rubber hardens can beaccelerated with special activators. Condensation cure two-component silicone rubbers are excellent for most general mold making and prototype applications. They are excellent for casting waxes, gypsum, epoxies and other plastics. GI-1220 is extremely useful for those applications where superior elongation and medium durometer are required.
| Главная Информация | |
|---|
| Характеристики | - Хорошая прочность на разрыв
- Низкая усадка
|
| Используется | |
| Формы | |
| Физический | Номинальное значение | Единица измерения | |
|---|
| Удельный вес | 1.08 | g/cm³ | |
| Усадка-
Вылеченный | 0.10 | % | |
| Тепловой | Номинальное значение | Единица измерения | |
|---|
| Service Temperature -
Cured | -51 to 171 | °C | |
| Cured Properties | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Покрытие-
Вылеченный | 0.925 | cm³/g | |
| Термокомплект | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Компоненты термокомплекта | | | |
| Hardener | Mix Ratio by Weight: 1.0
Mix Ratio by Volume: 11 | | |
| Resin | Mix Ratio by Weight: 10
Mix Ratio by Volume: 100 | | |
| Срок годности | 26 | wk | |
| Терморегулирующая вязкость 1 | 15000 to 25000 | cP | |
| Uncured Properties | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Цвет | | | |
| -- 2 | Blue | | |
| -- 3 | White | | |
| Вязкость | | | |
| -- 4 | 0.30 to 0.40 | Pa·s | |
| -- 5 | 30 to 40 | Pa·s | |
| Время отверждения | 16 to 18 | hr | |
| Срок службы горшка 6 | 90 to 150 | min | |
| Cured Properties | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость по суше | | | |
| Shore A 7 | 11 to 19 | | |
| Shore A 8 | 16 to 24 | | |
| Прочность на растяжение | 2.52 to 2.86 | MPa | ASTM D412 |
| Удлинение при разрыве | 450 to 500 | % | ASTM D412 |
| Tear Strength | 14.9 to 18.4 | kN/m | ASTM D624 |
| Примечание |
|---|
| 1 . | Mixed |
| 2 . | Activator |
| 3 . | Base |
| 4 . | Activator |
| 5 . | Base |
| 6 . | Mixed |
| 7 . | 1 Day |