Описание материалов:
TECATRON™ PPS is a high performance thermoplastic that combines good mechanical properties with excellent thermal and chemical resistance properties. There is no known solvent that dissolves TECATRON™ PPS at temperatures below 392°F. Its low ionic impurities make it an excellent choice for applications where high purity is a concern. TECATRON™ GF40 is a glass reinforced material that offers extremely high strength along with excellent chemical resistance properties. TECATRON™ PVX is a bearing grade PPS that is suitable for high load applications.
TECATRON™PPS's excellent thermal and chemical resistance along with its ionic impurities make an excellent choice for applications requiring low outgassing and high purity. TECATRON™PPS is typically used in the automotive, electrical/ electronic, industrial, mechanical, appliance and semiconductor industries.
| Главная Информация | |
|---|
| Характеристики | - Низкое (нет) содержание ионов
- Хорошая стабильность размеров
- Высокая чистота
- Высокая прочность
- Изоляция
- Хорошая коррозионная стойкость
- Хорошее сопротивление ползучести
- Хорошая химическая стойкость
|
| Используется | - Электрическое/электронное применение
- Электроприборы
- Промышленное применение
- Применение в автомобильной области
|
| Формы | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.35 | g/cm³ | ASTM D792 |
| Поглощение воды (23°C, 24 hr) | 0.020 | % | ASTM D570 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (M-Scale, 23°C) | 104 | | ASTM D785 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 3310 | MPa | ASTM D638 |
| Прочность на растяжение (Yield, 23°C) | 60.0 | MPa | ASTM D638 |
| Удлинение при растяжении (Break, 23°C) | 4.0 | % | ASTM D638 |
| Флекторный модуль (23°C) | 3000 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 120 | MPa | ASTM D790 |
| Коэффициент трения 1(vs. Itself - Dynamic) | 0.24 | | ASTM D1894 |
| Коэффициент износа (0.28 MPa, 0.25 m/sec) | 1100 | 10^-8 mm³/N·m | ASTM D3702 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact (23°C) | 27 | J/m | ASTM D256 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | ASTM D648 |
| 0.45 MPa, not annealed | 204 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 104 | °C | ASTM D648 |
| Температура плавления | 282 | °C | ASTM D2133 |
| CLTE-
Поток | 7.2E-5 | cm/cm/°C | ASTM D696 |
| Теплопроводность | 0.30 | W/m/K | |
| Максимальная рабочая температура-
Долгосрочный срок | 170 | °C | UL 746B |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Сопротивление громкости | 1.0E+15 | ohms·cm | ASTM D257 |
| Диэлектрическая постоянная 2(23°C, 60 Hz) | 3.00 | | ASTM D150 |
| Коэффициент рассеивания (23°C, 60 Hz) | 1.0E-4 | | ASTM D150 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость | V-0 | | UL 94 |
| Дополнительная информация |
|---|
| Data obtained from extruded shapes material. |
| Примечание |
|---|
| 1 . | 40 psi, 50 fpm |
| 2 . | 50% RH |