DOWLEX™ 2006G
| Категория | HDPE, Polyethylene Resin |
| Производитель | The Dow Chemical Company |
| Торговая марка | DOWLEX™ |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
SeU5lq_DOWLEX-2006G.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Dowlex™ 2006G Polyethylene Resin is an ethylene 1-octene copolymer, suitable for cast film applications and also perfectly designed to give excellent filler acceptance and low torque during compounding.
Dowlex™ 2006G offers superior stiffness and excellent temperature resistance making it the perfect partner for down gauging. Films produced using Dowlex™ 2006G offer low shrinkage which is ideal when registered printing is used.
Main Characteristics:
Complies with:
Dowlex™ 2006G offers superior stiffness and excellent temperature resistance making it the perfect partner for down gauging. Films produced using Dowlex™ 2006G offer low shrinkage which is ideal when registered printing is used.
Main Characteristics:
- Optimum extruder output and process ability, pure or in blends
- Superior stiffness and temperature resistance
Complies with:
- Europe Commission Regulation (EU) No 10/2011
- U.S. FDA 21 CFR 177.1520(c )3.2a
| Главная Информация | |
|---|---|
| Рейтинг агентства |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.961 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 20 | µm | |
| Прочность на растяжение | ASTM D882 | ||
| MD : Break, 20 µm | 38.0 | MPa | ASTM D882 |
| TD : Break, 20 µm | 19.0 | MPa | ASTM D882 |
| MD : 20 µm 1 | 21.0 | MPa | ASTM D882 |
| TD : 20 µm 2 | 15.0 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Break, 20 µm | 700 | % | ASTM D882 |
| TD : Break, 20 µm | 15 | % | ASTM D882 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm | 29 | g | ASTM D1922 |
| TD : 20 µm | 390 | g | ASTM D1922 |
| Инструкции по экструзии |
|---|
| Cast film extrusion conditions: Melt Temperature: 220°C Die gap: 0.7 mm Film thickness: 20 microns |
| Примечание | |
|---|---|
| 1 . | @ 5% Elongation |
| 2 . | @ 5% Elongation |
| Тип материала | Категория | Производитель |
|---|---|---|
| Kemcor HD 6095 Film | HDPE, MMW | Qenos Pty Ltd |
| SABIC® HDPE B6246 | HDPE | Saudi Basic Industries Corporation (SABIC) |
| SNOLEN® EF 0.21/46 HT | HDPE | JSC Gazprom neftekhim Salavat |
| UNIVAL™ DMDG-6240 NT 7 | HDPE | The Dow Chemical Company |
| EGYPTENE HD 5226 EA | HDPE | Sidpec (Sidi Kerir Petrochemicals Co.) |
| InnoPlus HD6600B | HDPE | PTT Global Chemical Public Company Limited |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved