LUVOTECH® 1850-9218

Категория	PBT, Polybutylene Terephthalate
Производитель	LEHVOSS Group
Торговая марка	LUVOTECH®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	SbNgZz_LUVOTECH18509218.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOTECH®1850-9218 is a polybutene terephthalate (PBT) material, which contains mineral fillers. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOTECH®The main features of 1850-9218 are:

anti-warping

Good stiffness

Typical application areas include:

engineering/industrial accessories

textile/fiber

Automotive Industry

business/office supplies

Главная Информация
Наполнитель/армирование	Минеральный наполнитель
Характеристики	Низкий уровень защиты Жесткий, хороший Хорошая прочность
Используется	Шестерня Текстильные изделия Инженерные аксессуары Применение в автомобильной области Бизнес-оборудование
Внешний вид	Черный

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.84	g/cm³	ISO 1183
Массовый расход расплава (MFR) (250°C/2.16 kg)	21	g/10 min	ISO 1133
Формовочная усадка	0.20 - 0.50	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 0.10	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	10000	MPa	ISO 527-2
Tensile Stress (Break)	61.0	MPa	ISO 527-2
Растяжимое напряжение (Yield)	1.3	%	ISO 527-2

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Charpy Unnotched Impact Strength (23°C)	14	kJ/m²	ISO 179/1eU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Температура непрерывного использования	130	°C	UL 746B
Максимальная рабочая температура- Короткий срок	180	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance	> 1.0E+10	ohms	IEC 60167
Удельное сопротивление поверхности	> 1.0E+10	ohms	IEC 60093

Инъекция	Номинальное значение	Единица измерения
Температура сушки
Hot air dryer, A	120	°C
Vacuum dryer, B	80	°C
Время сушки
Hot air dryer, A	4.0 - 6.0	hr
Vacuum dryer, B	6.0 - 8.0	hr
Задняя температура	240 - 260	°C
Средняя температура	260 - 280	°C
Передняя температура	250 - 270	°C
Температура сопла	250 - 265	°C
Температура обработки (расплава)	250	°C
Температура формы	60 - 120	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.02%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very quickly, the predried material should be fed to the processing immediately. Processing temperatures above 270°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.02%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very quickly, the predried material should be fed to the processing immediately. Processing temperatures above 270°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Тип материала	Категория	Производитель
PPR PBT01	PBT	Premier Plastic Resins, Inc.
ResMart Ultra PBT 23	PBT	ResMart
HONES® PBT GF30	PBT	Guangdong Shunde Hones Polymer Material Co., Ltd.
Beetle® PBTS145F	PBT	Teknor Apex Company (Chem Polymer)
4DUR® 9K22220	PBT	4Plas
Beetle® PBTS120S	PBT	Teknor Apex Company (Chem Polymer)

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

