Описание материалов:
EMAC resins adhere to and are compatible with a wide range of materials including paper, polyolefins, oriented polyolefins, polyesters, ionomers, PVdC, unplasticized PVC and other polar polymers. For use as heat seal layer, adhesive layer, or modifier for cost/performance enhancement. They are soft, pliable and tough at ambient and freezing temperatures and exhibit excellent ESCR. These polymers exhibit high solids fillability and compatibility with a wide range of polymers. This facilitates their uses as bases for all-purpose concentrates for addition to a wide spectrum of polymers. EMAC resins process like LDPE. EMAC+ Specialty Copolymers are produced under patented technology: US Patent 5804675.
| Главная Информация | |
|---|
| Характеристики | - Сополимер
- Хорошая прочность
- Высокий уровень ЭСКП (устойчивость к стрессу)
- Прочность при низкой температуре
- Мягкий
|
| Используется | - Пленка
- Медицинские/медицинские приложения
- Трубка
|
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.944 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 2.1 | g/10 min | ASTM D1238 |
| Содержание метилакрилата | 24.0 | wt% | |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore D) | 37 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение 1(Break) | 11.0 | MPa | ASTM D638 |
| Удлинение при растяжении 2(Break) | 840 | % | ASTM D638 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура ломкости | < -73.0 | °C | ASTM D746 |
| Викат Температура размягчения | 50.0 | °C | ASTM D1525 |
| Пиковая температура плавления | 77.0 | °C | ASTM D3418 |
| Примечание |
|---|
| 1 . | Type IV, 500 mm/min |
| 2 . | Type IV, 500 mm/min |