LUVOCOM® 1850-8282

Категория PBT, Polybutylene Terephthalate
Производитель Lehmann & Voss & Co.
Торговая марка LUVOCOM®
Порт Китай Шанхайский порт
Торговые условия FOB, CFR, CIF
Платежное средство L/C, T/T, Western Union
PDF SQttgc_LUVOCOM-1850-8282.pdf
Контактная информация
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Описание материалов:
LUVOCOM®1850-8282 is a polybutene terephthalate (PBT) material, and the filler is carbon fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 1850-8282 are:
  • chemical resistance
  • Conductivity
  • Electrostatic protection
  • Good stiffness

Typical application areas include:
  • textile/fiber
  • engineering/industrial accessories
  • Automotive Industry
  • business/office supplies
Главная Информация
Наполнитель/армирование
  • Армированный материал из углеродного волокна
Характеристики
  • Проводящий
  • Жесткий, хороший
  • Защита от электростатического разряда
  • Основа для защиты от растворителей
  • Хорошая прочность
  • Сопротивление щелочи
  • Стойкость к кислоте
  • Устойчивость к углеводородам
  • Маслостойкость
  • Сопротивление смазке и маслу
Используется
  • Текстильные изделия
  • Инженерные аксессуары
  • Применение в автомобильной области
  • Бизнес-оборудование
Внешний вид
  • Черный
ФизическийНоминальное значениеЕдиница измеренияМетод испытания
Плотность 1.42g/cm³ISO 1183
Формовочная усадка 0.20 - 0.60%DIN 16901
Поглощение воды (23°C, 24 hr)< 0.10%
МеханическиеНоминальное значениеЕдиница измеренияМетод испытания
Модуль растяжения 16000MPaISO 527-2
Tensile Stress (Break)130MPaISO 527-2
Растяжимое напряжение (Yield)1.8%ISO 527-2
Флекторный модуль 14000MPaISO 178
Флекторный стресс 190MPaISO 178
Flexural Strain at Flexural Strength 2.3%ISO 178
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Максимальная рабочая температура- Короткий срок 180°C
ЭлектрическийНоминальное значениеЕдиница измеренияМетод испытания
Insulation Resistance ohmsIEC 60167
ВоздействиеНоминальное значениеЕдиница измеренияМетод испытания
Charpy Unnotched Impact Strength (23°C)35kJ/m²ISO 179/1eU
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Heat Deflection Temperature (1.8 MPa, Unannealed)195°CISO 75-2/A
Температура непрерывного использования 130°CUL 746B
ЭлектрическийНоминальное значениеЕдиница измеренияМетод испытания
Удельное сопротивление поверхности < 1.0E+5ohmsIEC 60093
ИнъекцияНоминальное значениеЕдиница измерения
Температура сушки
    A 120°C
    Vacuum dryer, B 80.0°C
Время сушки
    A 4.0 - 6.0hr
    Vacuum dryer, B 6.0 - 8.0hr
Рекомендуемая максимальная влажность 0.020%
Задняя температура 240 - 260°C
Средняя температура 260 - 280°C
Передняя температура 250 - 270°C
Температура сопла 250 - 265°C
Температура обработки (расплава) 250°C
Температура формы 60.0 - 120°C
Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.02%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very quickly, the predried material should be fed to the processing immediately. Processing temperatures above 270°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.
Тип материала Категория Производитель
Ranger PBT PBT-403-M-G0 HF PBT Beijing Ranger Chemical Co., Ltd.
SCHULADUR® A GB 30 SCHWARZ PBT A. Schulman Europe
NOVADURAN® 5010GN6-30 PBT Mitsubishi Engineering-Plastics Corp
HiFill FR® PBT GF30 FR-S PBT Techmer Engineered Solutions
VALOX™ 855 resin PBT SABIC Innovative Plastics
MALAT 37GW200H - 9430 PBT AD majoris
Получите информацию об этом продукте следующим способом.
Телефон+086 13424755533
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Copyright © russianpolymer.com All Rights Reserved
Получите информацию об этом продукте следующим способом.
+08613424755533
sales@su-jiao.com

Служба поддержки клиентов Вичат
Свяжитесь с нами