Описание материалов:
Menzolit® BMC 1400 is a bulk moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is injection moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens nor any heavy metals.
Menzolit® BMC 1400 is a special BMC for the use on an engine. The glass content is set to a level that combines good mouldability with good strength and stiffness properties. The product has been developped fot high resistance against gasoline, lubricants, cooling agents or cleaning agents that are used around an automotive engine. Because of its resin matrix it is especially resistant to cyclic loads under elevated temperature. Typical applications are valve covers, gear box covers, carburator housings, or housings for auxiliary motors.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Стекло \ Mineral, 25% наполнитель по весу
|
| Характеристики | - Огнестойкий
- Хорошая химическая стойкость
- Хорошая плавность
- Хорошая жесткость
- Хорошая прочность
- Без галогенов
- Высокая термостойкость
- Устойчивость к углеводородам
- Низкий уровень дыма
|
| Используется | - Автомобильная крышка под капот
- Корпус электродвигателя
|
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Код маркировки деталей (ISO 11469) | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 1.90 | g/cm³ | ISO 1183 |
| Формовочная усадка | | | |
| -- | 0.30 | % | ISO 2577 |
| -- 1 | 0.0 | % | DIN 53464 |
| Поглощение воды (Saturation, 23°C) | < 0.30 | % | ISO 62 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения (Compression Molded) | 13000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 37.0 | MPa | ISO 527-2 |
| Флекторный модуль (Compression Molded) | 10000 | MPa | ISO 178 |
| Флекторный стресс (Compression Molded) | 125 | MPa | ISO 178 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность (Compression Molded) | 35 | kJ/m² | ISO 179 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 150 | °C | ISO 75-2/A |
| Температура непрерывного использования | 170 | °C | Internal Method |
| Температура перехода стекла | 162 | °C | DSC |
| CLTE-
Поток | 1.0E-5 | cm/cm/°C | ISO 11359-2 |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельное сопротивление поверхности | 1.0E+12 | ohms | IEC 60093 |
| Сопротивление громкости | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость (3.00 mm) | HB | | UL 94 |
| Температура зажигания провода свечения | 750 | °C | IEC 60695-2-13 |
| Индекс кислорода | 22 | % | ISO 4589-2 |
| Дополнительная информация | Номинальное значение | | Метод испытания |
|---|
| Glow Bar | Level BH 2 <= 95 | | IEC 60707-3 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 135 to 160 | °C | |
| Давление впрыска | 2.00 to 8.00 | MPa | |
| Примечание |
|---|
| 1 . | Post Molding Shrinkage |