SABIC® PPcompound 2500-6
| Категория | PP, Polypropylene , PP, Unspecified |
| Производитель | Saudi Basic Industries Corporation (SABIC) |
| Торговая марка | SABIC® PPcompound |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
RpTwDf_SABIC-PPcompound-2500-6.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
SABIC® PPcompound 2500/6 is a mineral filled modified polypropylene. Typical material properties include very high flow, high impact, good stiffness and low shrinkage and CLTE. Typical material properties also include good chemical resistance and esthetical performance. Typical applications include automotive exterior trims such as lateral siding, bumper strips and bumpers. It can be used in painted and unpainted applications with UV
stabilization added on demand.
SABIC® PPcompound 2500/6 is a designated automotive grade.
stabilization added on demand.
SABIC® PPcompound 2500/6 is a designated automotive grade.
| Главная Информация | |
|---|---|
| Наполнитель/армирование |
|
| Добавка |
|
| Характеристики |
|
| Используется |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.960 | g/cm³ | ISO 1183 |
| Массовый расход расплава (MFR) (230°C/2.16 kg) | 30 | g/10 min | ISO 1133 |
| Формовочная усадка (24 hr) | 0.80 | % | Internal Method |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 19.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 15.0 | MPa | |
| Растяжимое напряжение (Break, 3.20 mm, Injection Molded) | > 400 | % | ISO 527-2/5/50 |
| Флекторный модуль 1(Injection Molded) | 1100 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Ударная прочность (23°C, Injection Molded) | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength (-40°C, Injection Molded) | No Break | ISO 179/1eU | |
| Зубчатый изод ударная прочность | ISO 180/4A | ||
| -20°C, Injection Molded | 15 | kJ/m² | |
| 0°C, Injection Molded | No Break | ||
| 23°C, Injection Molded | No Break |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 90.0 | °C | ISO 75-2/B |
| Викат Температура размягчения | 125 | °C | ISO 306/A |
| CLTE- Поток | ASTM D696 | ||
| -30 to 30°C | 6.0E-5 | cm/cm/°C | |
| 23 to 80°C | 9.0E-5 | cm/cm/°C |
| Примечание | |
|---|---|
| 1 . | Method I (3 point load) |
| Тип материала | Категория | Производитель |
|---|---|---|
| POLYFORT® FPP 1220 | PP, Unspecified | A. Schulman Inc. |
| ALTECH® PP-H ECO 4940/500 MR40 | PP Homopolymer | ALBIS PLASTIC GmbH |
| Osterlene® PPH20NA | PP Homopolymer | Osterman & Company |
| INNOPOL® PP CS 2-2130 TA | PP Impact Copolymer | Inno-Comp Ltd. |
| ALTECH® PP-H A 2440/550 GF25 MR15 CP | PP Homopolymer | ALBIS PLASTIC GmbH |
| Golden Compound PP S²PC 3545 BO 10IM16 | PP, Unspecified | Golden Compound GmbH |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved