LUVOCOM® 7-0755

Категория PA610, Polyamide 610 , Nylon 610
Производитель Lehmann & Voss & Co.
Торговая марка LUVOCOM®
Порт Китай Шанхайский порт
Торговые условия FOB, CFR, CIF
Платежное средство L/C, T/T, Western Union
PDF RbgbCA_LUVOCOM-7-0755.pdf
Контактная информация
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Описание материалов:
LUVOCOM®7-0755 is a polyamide 610 (nylon 6/10) material, and the filler is glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 7-0755 are:
  • High stiffness
  • high strength
  • Good dimensional stability
  • moisture resistance
  • Wear-resistant

Typical application areas include:
  • engineering/industrial accessories
  • textile/fiber
  • Automotive Industry
  • business/office supplies
  • Handle
Главная Информация
Наполнитель/армирование
  • Армированный стекловолокном материал
Добавка
  • Ptfe лубрикант
Характеристики
  • Хорошая стабильность размеров
  • Низкий коэффициент трения
  • Жесткий, высокий
  • Высокая прочность
  • Хорошая стойкость к истиранию
  • Смазка
  • Низкий или не впитывающий
Используется
  • Ручка
  • Текстильные изделия
  • Инженерные аксессуары
  • Машина/механические детали
  • Применение в автомобильной области
  • Бизнес-оборудование
  • Подшипник
Внешний вид
  • Натуральный цвет
ФизическийНоминальное значениеЕдиница измеренияМетод испытания
Плотность 1.41g/cm³ISO 1183
Формовочная усадка 0.20 - 0.40%DIN 16901
Поглощение воды (23°C, 24 hr)< 0.15%
МеханическиеНоминальное значениеЕдиница измеренияМетод испытания
Модуль растяжения 11000MPaISO 527-2
Tensile Stress (Break)200MPaISO 527-2
Растяжимое напряжение (Yield)3.5%ISO 527-2
Флекторный модуль 9000MPaISO 178
Флекторный стресс 290MPaISO 178
Коэффициент трения
    Dynamic 0.35
    Static 0.25
Flexural Strain at Flexural Strength 4.0%ISO 178
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Максимальная рабочая температура- Короткий срок 140°C
ЭлектрическийНоминальное значениеЕдиница измеренияМетод испытания
Insulation Resistance > 1.0E+12ohmsIEC 60167
ВоздействиеНоминальное значениеЕдиница измеренияМетод испытания
Charpy Unnotched Impact Strength
    -30°C 85kJ/m²ISO 179/1fU
    23°C 100kJ/m²ISO 179/1eU
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Heat Deflection Temperature (1.8 MPa, Unannealed)210°CISO 75-2/A
Температура непрерывного использования 90.0°CUL 746B
CLTE- Поток 4.0E-5cm/cm/°CDIN 53752
Теплопроводность 0.30W/m/KDIN 52612
ИнъекцияНоминальное значениеЕдиница измерения
Температура сушки
    A 75.0°C
    B 105°C
Время сушки- A 6.0 - 10hr
Рекомендуемая максимальная влажность 0.10%
Задняя температура 240 - 270°C
Средняя температура 260 - 280°C
Передняя температура 270 - 290°C
Температура сопла 270 - 290°C
Температура обработки (расплава) 265°C
Температура формы 70.0 - 100°C
Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water very rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.
Тип материала Категория Производитель
Shandong PA610 A6G9301-G Nylon 610 Shandong Dongchen Engineering Plastics Co., Ltd.
Badamid® PA610 GF30 Nylon 610 Bada AG
TECHNYL eXten® D 219WFC V50 BLACK Nylon 610 Solvay Engineering Plastics
INELEC PA610CF30 Nylon 610 Infinity LTL Engineered Compounds
LNP™ LUBRICOMP™ QFL17RS compound Nylon 610 SABIC Innovative Plastics
LNP™ LUBRICOMP™ QFL32 compound Nylon 610 SABIC Innovative Plastics
Получите информацию об этом продукте следующим способом.
Телефон+086 13424755533
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Copyright © russianpolymer.com All Rights Reserved
Получите информацию об этом продукте следующим способом.
+08613424755533
sales@su-jiao.com

Служба поддержки клиентов Вичат
Свяжитесь с нами