Описание материалов:
INTEGRAL™ 709 is a multipurpose, low melt, low viscosity film designed to act as the tie layer between porous substrates, (e.g., fabric to foam adhesion). INTEGRAL 709 is available corona treated (with manufacturing approval).
New experimental films are continually being developed. Please discuss your particular application needs with your Dow representative.
General Characteristics:
New experimental films are continually being developed. Please discuss your particular application needs with your Dow representative.
General Characteristics:
- Heat Activation Point: 185°F (85°C)
- Yield: 205 sq ft/lb/mil (41.9 m²/kg/25 µm)
- Available Colors: Clear
- Gauge Range: 2.0-8.0 mil (50-200 µm)
- Width Range: 12-76 in (304-1930 mm)
| Главная Информация | |
|---|---|
| Внешний вид |
|
| Формы |
|
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 51 100 | µm | |
| Толщина пленки-рекомендовано/доступно | 2.0-8.0 mil (50-200 µ) | ||
| Сектантный модуль | ASTM D882 | ||
| 2% Secant, MD : 51 µm | 107 | MPa | |
| 2% Secant, MD : 100 µm | 86.2 | MPa | |
| 2% Secant, TD : 51 µm | 121 | MPa | |
| 2% Secant, TD : 100 µm | 103 | MPa | |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield, 51 µm | 9.65 | MPa | |
| MD : Yield, 100 µm | 9.65 | MPa | |
| TD : Yield, 51 µm | 8.27 | MPa | |
| TD : Yield, 100 µm | 8.27 | MPa | |
| MD : Break, 51 µm | 19.7 | MPa | |
| MD : Break, 100 µm | 19.7 | MPa | |
| TD : Break, 51 µm | 12.4 | MPa | |
| TD : Break, 100 µm | 11.7 | MPa | |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Break, 51 µm | 200 | % | |
| MD : Break, 100 µm | 350 | % | |
| TD : Break, 51 µm | 400 | % | |
| TD : Break, 100 µm | 350 | % | |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 30 | g | |
| MD : 100 µm | 80 | g | |
| TD : 51 µm | 250 | g | |
| TD : 100 µm | 500 | g | |
| Ширина пленки | 30.48 to 193.04 | cm | |
| Выход (25.0 µm) | 41.9 | m²/kg |
| Тепловой | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Температура активации тепла | 85 | °C |
| Тип материала | Категория | Производитель |
|---|---|---|
| DOW™ Medical Packaging Films 2000 | Polyolefin, Unspecified | The Dow Chemical Company |
| Flexathene® TP4310HR | Polyolefin, Unspecified | LyondellBasell Industries |
| DynaChar™ 3522 | Polyolefin, Unspecified | Polymer Dynamix |
| Hyundai EP Breathable AT900/2102 | Polyolefin, Unspecified | HYUNDAI EP Co., Ltd. |
| CALP FR913-1 | Polyolefin, Unspecified | Lion Idemitsu Composites Co., Ltd. |
| Softell TKG 442N C12507 | Polyolefin, Unspecified | LyondellBasell Industries |
Получите информацию об этом продукте следующим способом.