Описание материалов:
Menzolit® SMC 1400 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens nor heavy metals.
Menzolit® SMC 1400 is a special SMC being used in the environment of a combustion engine. The glass level has been selected to combine good mouldability with good stiffness and strength properties. The product shows an excellent resistance to common fuels, lubricants, cooling liquids and cleaning materials. Because of its specific matrix resin it is suitable for cyclic loads at higher service temperatures. Typical applications are valve covers, camshaft drive covers, gear box covers as well as oil pans or housings for auxiliary drive systems.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Стекло \ минеральное, 35% наполнитель по весу
|
| Характеристики | - Огнестойкий
- Хорошая плавность
- Хорошая жесткость
- Без галогенов
- Высокая термостойкость
- Высокая прочность
- Низкий уровень дыма
|
| Используется | - Автомобильные Приложения
- Клапаны/Детали Клапана
|
| Внешний вид | |
| Формы | - Smc-лист формовочный состав
|
| Метод обработки | |
| Код маркировки деталей (ISO 11469) | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 1.90 | g/cm³ | ISO 1183 |
| Формовочная усадка | | | |
| -- 1 | 0.0 | % | DIN 53464 |
| -- | 0.030 | % | ISO 2577 |
| Поглощение воды (Saturation, 23°C) | < 0.30 | % | ISO 62 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения (Compression Molded) | 10000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 130 | MPa | ISO 527-2 |
| Растяжимое напряжение (Break, Compression Molded) | 1.6 | % | ISO 527-2 |
| Флекторный модуль (Compression Molded) | 10000 | MPa | ISO 178 |
| Флекторный стресс (Compression Molded) | 250 | MPa | ISO 178 |
| Сжимающее напряжение | 140 | MPa | ISO 14126 |
| Poisson's Ratio | 0.30 | | Internal Method |
| Matrix Crazing Strain | 0.50 | % | Internal Method |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность (Compression Molded) | 100 | kJ/m² | ISO 179 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | °C | ISO 75-2/A |
| Температура непрерывного использования | 170 | °C | Internal Method |
| Температура перехода стекла | 162 | °C | DSC |
| CLTE-
Поток | 1.2E-5 | cm/cm/°C | ISO 11359-2 |
| Воспламеняемость | Номинальное значение | | Метод испытания |
|---|
| Огнестойкость (3.00 mm) | HB | | UL 94 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 135 to 160 | °C | |
| Давление впрыска | 8.00 to 10.0 | MPa | |
| Примечание |
|---|
| 1 . | Post Molding Shrinkage |