KRATON® D1114 P
| Категория | SIS, Styrene Isoprene Styrene Block Copolymer |
| Производитель | Kraton Polymers LLC |
| Торговая марка | KRATON® |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
QyZ9S9_KRATON-D1114-P.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Kraton D1114 P is a clear, linear triblock copolymer based on styrene and isoprene with a polystyrene content of 19%. It is suppliedfrom North America in the physical form identified below.
Kraton D1114 P is used as an ingredient in formulating adhesives, sealants and coatings. It may also find use as a modifier of bitumen or thermoplastics and in compound formulations.
- Kraton D1114 PT - supplied as a dusted dense pellet
- Kraton D1114 PSM - supplied as a powder dusted with silica
Kraton D1114 P is used as an ingredient in formulating adhesives, sealants and coatings. It may also find use as a modifier of bitumen or thermoplastics and in compound formulations.
| Главная Информация | |
|---|---|
| Добавка |
|
| Характеристики |
|
| Используется |
|
| Внешний вид |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.920 | g/cm³ | ASTM D4025 |
| Массовый расход расплава (MFR) (200°C/5.0 kg) | 7.0 to 13 | g/10 min | ASTM D1238 |
| Антиоксидантная добавка 1 | 0.080 to 0.30 | % | Internal Method |
| Содержание золы | |||
| PSM 2 | 2.5 to 5.0 | % | ISO 247 |
| Talc | 0.2 to 0.4 | wt% | Internal Method |
| Содержание полистирола | 17 to 21 | % | Internal Method |
| Вязкость раствора- Толуол, 25% Вт (25 °C) | 600 to 1000 | mPa·s | Internal Method |
| Общее количество экстрактов | < 1.0 | % | Internal Method |
| Летучее вещество | < 0.50 | % | Internal Method |
| Дополнительная информация | Номинальное значение | ||
|---|---|---|---|
| Содержимое блока | < 1.00 | ||
| Styrene/Rubber ratio | 19/81 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Tensile Stress (300% Strain) | 1.86 | MPa | ASTM D412 |
| Прочность на растяжение (Yield) | 31.7 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 1300 | % | ASTM D412 |
| Примечание | |
|---|---|
| 1 . | Primary antioxidant is a non-staining, phenolic antioxidant. The antioxidant package also contains a non-TNPP secondary antioxidant at a target level of 0.2% wt. |
| 2 . | The final dusting level is a combination of the talc from the original D1114 PT and silica added during the milling process. |
| Тип материала | Категория | Производитель |
|---|---|---|
| KRATON® D1117 P | SIS | Kraton Polymers LLC |
| VECTOR® 4113 | SIS | Dexco Polymers LP |
| VECTOR® 4211N | SIS | TSRC Corporation |
| KRATON® D1183 P | SIS | Kraton Polymers LLC |
| KRATON® D4433 P | SIS | Kraton Polymers LLC |
| KRATON® D1113 P | SIS | Kraton Polymers LLC |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved