POLYTROPE® STR 2030REU-01 NATURAL
Описание материалов:
POLYTROPE STR 2030REU is a flame retardant TPO resin which is UL 94 V-0 and 5VA compliant, RoHS compliant, and specifically designed to provide high melt strength for extrusion, and thermoforming processes. It is non-blooming, and provides balanced impact resistance with stiffness, making it especially suitable for panel and closure applications requiring flame retarding properties. It can be extruded in smooth or textured surfaces, or co-extruded with a POLYTROPE STR enhanced polyolefin cap resin to further customize its' durability, appearance, or feel for interior and exterior applications. The capability of POLYTROPE STR 2030REU to provide an exceptionally smooth surface in extrusion and thermoforming makes it well suited to lamination processes with decorative films. It is also easily colored and is paintable by standard TPO paint systems.
| Главная Информация | |
|---|
| Характеристики | - Огнестойкий
- Хорошая прочность расплава
- Хорошая устойчивость к погоде
- Низкий CLTE
- Болезненный
- Перерабатываемый материал
|
| Рейтинг агентства | |
| Формы | |
| Метод обработки | - Коэкструзия
- Экструзия
- Экструзионный профиль
- Экструзионный лист
- Термоформовка
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес 1 | 1.31 | g/cm³ | ISO 1183 |
| Массовый расход расплава (MFR) (230°C/2.16 kg) | 0.80 | g/10 min | ISO 1133 |
| Формовочная усадка (23°C, 24 hr, 3.18 mm) | 0.80 to 1.2 | % | ISO 294-4 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress 2(Yield, 23°C) | 19.0 | MPa | ISO 527-2 |
| Растяжимое напряжение 3(Break, 233°C) | 430 | % | ISO 527-2 |
| Флекторный модуль-
Аккорд 4(23°C) | 1930 | MPa | ISO 178 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact-
Поток | | | ASTM D256 |
| -30°C, 3.18 mm, Injection Molded | 32 | J/m | |
| 23°C, 3.18 mm, Injection Molded | 430 | J/m | |
| Ударное устройство для дротиков (-9°C, Total Energy, Ductile Failure) | 35.0 | J | ASTM D3763 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 90.6 | °C | ISO 75-2/Bf |
| CLTE-
Поток (-30 to 100°C) | 5.4E-5 | cm/cm/°C | ASTM E831 |
| Воспламеняемость | Номинальное значение | | Метод испытания |
|---|
| Огнестойкость | | | UL 94 |
| 3.18 mm, All Colors | HB | | |
| 1.59 mm, All Colors | V-0
5VA | | |
| Оптический | Номинальное значение | | Метод испытания |
|---|
| Блестящий Гарднер (60°, 3180 µm, Thermoformed, Smooth) | 20 to 40 | | ISO 2813 |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Sag -
8 inch span, two point support (149°C, 3.20 mm) | 0.00 | mm | ASTM D3769 |
| Примечание |
|---|
| 1 . | Method A |
| 2 . | Type 1, 50 mm/min |
| 3 . | Type 1, 50 mm/min |
| 4 . | Type 1A, 2.0 mm/min |