Описание материалов:
Andur 80-5AP is a polyether (PTMG) based liquid, toluene diisocyanate terminated prepolymer. An elastomer with a hardness of 83-85 Shore A is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by curing Andur 80-5AP with polyols and their combination with Curene 442 and other diamines, or through the use of plasticizers.
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 1.05 | g/cm³ | ASTM D1505 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore A) | 83 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на сжатие | | | ASTM D695 |
| 5% strain | 0.676 | MPa | ASTM D695 |
| 10% strain | 1.68 | MPa | ASTM D695 |
| 15% strain | 2.87 | MPa | ASTM D695 |
| 25% strain | 4.38 | MPa | ASTM D695 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ASTM D412 |
| 100% strain | 5.38 | MPa | ASTM D412 |
| 300% strain | 9.69 | MPa | ASTM D412 |
| Прочность на растяжение (Yield) | 36.5 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 580 | % | ASTM D412 |
| Комплект сжатия | 28 | % | ASTM D395B |
| Сопротивляемость Bayshore | 55 | % | ASTM D2632 |
| Термокомплект | Номинальное значение | Единица измерения | |
|---|
| Срок службы горшка | 6.0 - 7.0 | min | |
| Время демолд | 30 | min | |
| Время доставки (96°C) | 16 | hr | |
| Дополнительная информация |
|---|
| Durometer Hardness, ASTM D2240, Shore A: 81 to 85Die C Tear, ASTM D1004: 425 pliAverage Split Tear, ASTM D1938: 130 pliStoichiometry Curative Level: 95%Mix Temperature:
Andur 80-5 AP: 180-212°F
Curene 442: 235-250°F |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 104 - 113 | °C | |