Описание материалов:
APTIV® 2000 series films are the unfilled amorphous films made from VICTREX® PEEK™ polymer. The film provides a material solution for engineers in ultra-high performance applications.
APTIV films are a comprehensive range of versatile, high-performance films, the use of which can facilitate reduced systems costs, improved performance and enhanced design freedom.
APTIV 2000 has a unique combination of properties providing high temperature performance, light weight, mechanical strength, durability, excellent radiation, hydrolysis and chemical resistance, electrical insulation, wear and abrasion resistance, excellent barrier properties with high purity, good flammability without the use of flame retardants, low toxicity of combustion products, and low moisture absorption in a film format. Inherently halogen free and ease of processing makes APTIV films a technology enabler for our customers and end users.
Please note - APTIV 2000 will crystallize if taken above the Tg (143°C, 289°F) in either secondary processes or end use application. The crystallization is not reversible back to the amorphous phase without re-melting the material. Consideration of the temperature range during processing and end use application needs to be included if selecting APTIV 2000.
| Главная Информация | |
|---|
| Характеристики | - Аморфный
- Барьерная смола
- Чистота/Высокая чистота
- Прочный
- Электрически изолирующий
- Отличная Печатающая способность
- Огнестойкий
- Хорошая стойкость к истиранию
- Хорошая химическая стойкость
- Хорошая технологичность
- Хорошая прочность
- Хорошая износостойкость
- Без галогенов
- Термогерметичный
- Высокая термостойкость
- Высокая прочность
- Устойчивость к гидролизу
- Низкое поглощение влаги
- Низкий уровень дыма
- Низкая токсичность
- Металлизируемый
- Устойчивость к излучению (гамма)
- Перерабатываемый материал
- Свариваемый
|
| Используется | - Аэрокосмическое применение
- Уплотнение
- Диафрагмы
- Электрические детали
- Пленка
- Изоляция
- Ламинаты
- Печатные платы
|
| Рейтинг агентства | - ЕС 2002/72/ЕС
- ЕС 2004/19/ЕС
- Управление по санитарному надзору за качеством пищевых продуктов и медикаментов 21 CFR 177,2415
|
| Соответствие RoHS | |
| Формы | |
| Метод обработки | - Покрытие
- Ламинирование
- Термоформовка
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность (23°C) | 1.26 | g/cm³ | ISO 1183 |
| Поглощение воды 1(Equilibrium, 23°C, 0.0500 mm, 50% RH) | 0.21 | % | ISO 62 |
| Усадка 2 | | | |
| MD
: 200°C, 50.0 µm | < 10 | % | |
| TD
: 200°C, 50.0 µm | < 5.0 | % | |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Dielectric Breakdown | | | ASTM D149 |
| 23°C, 25.0 µm | 6750 | V | |
| 23°C, 50.0 µm | 9500 | V | |
| 23°C, 125.0 µm | 15000 | V | |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Сопротивление проколу (23 °C, 50,0 мкм) | 40.0 | kJ/m² | Internal Method |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки-рекомендовано/доступно | 6 to 300 µm | | |
| Модуль растяжения | | | ISO 527-3 |
| MD
: 23°C, 25 µm | 1800 | MPa | |
| TD
: 23°C, 25 µm | 1800 | MPa | |
| MD
: 23°C, 50 µm | 1800 | MPa | |
| TD
: 23°C, 50 µm | 1800 | MPa | |
| MD
: 23°C, 100 µm | 1600 | MPa | |
| TD
: 23°C, 100 µm | 1600 | MPa | |
| Tensile Stress | | | ISO 527-3 |
| MD
: Break, 23°C, 25 µm | 130 | MPa | |
| TD
: Break, 23°C, 25 µm | 130 | MPa | |
| MD
: Break, 23°C, 50 µm | 120 | MPa | |
| TD
: Break, 23°C, 50 µm | 120 | MPa | |
| MD
: Break, 23°C, 100 µm | 120 | MPa | |
| TD
: Break, 23°C, 100 µm | 120 | MPa | |
| Удлинение при растяжении | | | ISO 527-3 |
| MD
: Break, 23°C, 25 µm | > 200 | % | |
| TD
: Break, 23°C, 25 µm | > 200 | % | |
| MD
: Break, 23°C, 50 µm | > 200 | % | |
| TD
: Break, 23°C, 50 µm | > 200 | % | |
| MD
: Break, 23°C, 100 µm | > 200 | % | |
| TD
: Break, 23°C, 100 µm | > 200 | % | |
| Сопротивление разрыву брюк 3 | | | ISO 6383-1 |
| MD
: 50 µm | 6.00 | N/mm | |
| TD
: 50 µm | 6.00 | N/mm | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Пиковая температура кристаллизации (DSC) | 143 | °C | |
| CLTE-
Поток 4(0.0500 mm) | 6.0E-5 | cm/cm/°C | ASTM D696 |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Сопротивление громкости 5(23°C, 0.0500 mm) | 2.0E+16 | ohms·cm | ASTM D257 |
| Диэлектрическая прочность | | | ASTM D149 |
| 23°C, 0.0250 mm | 270 | kV/mm | |
| 23°C, 0.0500 mm 6 | 190 | kV/mm | |
| 23°C, 0.100 mm | 120 | kV/mm | |
| Диэлектрическая постоянная (23°C, 0.0500 mm, 10 MHz) | 3.30 | | ASTM D150 |
| Коэффициент рассеивания (23°C, 0.0500 mm, 10 MHz) | 3.0E-3 | | ASTM D150 |
| Примечание |
|---|
| 1 . | 24 hrs |
| 2 . | TM-VX-84 |
| 3 . | 23°C |
| 4 . | below Tg |
| 5 . | 100 V |
| 6 . | 6.35 mm electrode |