Alkathene® XLF197
| Категория | LLDPE, Linear Low Density Polyethylene |
| Производитель | Qenos Pty Ltd |
| Торговая марка | Alkathene® |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
QEYZPq_Alkathene-XLF197.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
XLF197 is a low density polyethylene designed for the production of thin gauge (less than 20µm) high clarity films. XLF197 does not contain any additives.
XLF197 is intended primarily for the manufacture of food wrap films; often an additive is incorporated during the manufacture of film to enhance cling performance.
XLF197 is intended primarily for the manufacture of food wrap films; often an additive is incorporated during the manufacture of film to enhance cling performance.
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.920 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 5.5 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 15 | µm | |
| Сектантный модуль | ASTM D882 | ||
| 2% secant, MD : 15 µm, blown film | 180 | MPa | ASTM D882 |
| 2% secant, TD : 15 µm, blown film | 220 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield, 15 µm, blown film | 12.0 | MPa | ASTM D882 |
| TD : Yield, 15 µm, blown film | 11.0 | MPa | ASTM D882 |
| MD : Broken, 15 µm, blown film | 28.0 | MPa | ASTM D882 |
| TD : Broken, 15 µm, blown film | 13.0 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Broken, 15 µm, blown film | 150 | % | ASTM D882 |
| TD : Broken, 15 µm, blown film | 630 | % | ASTM D882 |
| Ударное падение Dart (15 µm, Blown Film) | 45 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 15 µm, blown film | 190 | g | ASTM D1922 |
| TD : 15 µm, blown film | 82 | g | ASTM D1922 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45 °, 15.0 µm, blown film) | 76 | ASTM D2457 | |
| Haze (15.0 µm, blown film) | 4.0 | % | ASTM D1003 |
| Дополнительная информация |
|---|
| Film properties taken from blown film processed at a blow up ratio of 2:1. |
| Тип материала | Категория | Производитель |
|---|---|---|
| MarFlex® 7109FJ | LLDPE | Chevron Phillips Chemical Company LLC |
| Braskem PE HF3712 | LLDPE | Braskem |
| ExxonMobil™ LLDPE LL 3001.63 | LLDPE | ExxonMobil Chemical |
| DOWLEX™ 2045.11G | LLDPE | The Dow Chemical Company |
| Flexirene® FG 30 | LLDPE | Versalis S.p.A. |
| Ravago Compounds HMP-304 (Roto) | LLDPE | Ravago Manufacturing Americas, LLC |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved