Описание материалов:
Makrolon® AR sheet is an abrasion and enhanced UV resistant polycarbonate sheet that offers glasslike hardness coupled with the impact strength of standard polycarbonate. Additionally, Makrolon® AR offers on both surfaces enhanced resistance against yellowing and hazing for an extended service life in high profile architectural glazing. Makrolon® AR has a 10-years warranty against breakage and 5-years warranty against delamination and weathering.
Applications:
Typical applications for Makrolon® AR sheet include transparent sound barriers, school and hospital shelter glazing. Makrolon® AR is also used extensively in correctional and psychiatric facilities. Additionally, the product performs well for view windows and machine guards in harsh chemical environments. Due to its scratch-resistant coating, Makrolon® AR cannot be formed like other Makrolon® sheets.
| Главная Информация | |
|---|
| Характеристики | - Высокая ударопрочность
- Хорошая устойчивость к ультрафиолетовому излучению
- Хорошая стойкость к истиранию
- Хорошая устойчивость к погоде
- Высокое разрешение
|
| Используется | |
| Формы | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 1.20 | g/cm³ | ISO 1183 |
| Поглощение воды | | | ISO 62 |
| Saturated, 23°C | 0.30 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.12 | % | ISO 62 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 2350 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | > 60.0 | MPa | ISO 527-2/50 |
| Растяжимое напряжение (Yield) | 6.0 | % | ISO 527-2/50 |
| Номинальное растяжение при разрыве | > 50 | % | ISO 527-2/50 |
| Флекторный модуль 1 | 2350 | MPa | ISO 178 |
| Флекторный стресс 2 | 90.0 | MPa | ISO 178 |
| Износостойкость-
Delta Haze | | | |
| -- 3 | 1 - 4 | % | ASTM D1044 |
| -- 4 | 4 - 9 | % | ANSI Z26.1 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность 5(23°C, Partial Break) | 80 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | | ISO 179/1eU |
| Зубчатый изод Impact 6(23°C, Partial Break) | 90 | kJ/m² | ISO 180/A |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature | | | |
| 0.45 MPa, not annealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 128 | °C | ISO 75-2/A |
| Викат Температура размягчения | 148 | °C | ISO 306/B50 |
| CLTE-
Поток (23 to 55°C) | 6.5E-5 | cm/cm/°C | ISO 11359-2 |
| Теплопроводность (23°C) | 0.20 | W/m/K | ISO 8302 |
| Воспламеняемость | Номинальное значение | | Метод испытания |
|---|
| Огнестойкость | | | UL 94 |
| > 1.5 mm, ALL | HB | | UL 94 |
| 0.8 to 1.4mm, ALL | V-2 | | UL 94 |
| > 10.0 mm, Clear 8099 | V-0 | | UL 94 |
| Оптический | Номинальное значение | | Метод испытания |
|---|
| Индекс преломления 7 | 1.587 | | ISO 489 |
| Примечание |
|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 100 cycles, 500 g, CS-10F Wheel |
| 4 . | 500 cycles, 500 g, CS-10F Wheel |
| 5 . | 3 mm |
| 6 . | 3.2 mm |
| 7 . | Method A |