OxyShield® 2545

Категория	PA6, Polyamide 6 , Nylon 6
Производитель	Honeywell
Торговая марка	OxyShield®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	PgCnUI_OxyShield-2545.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

OxyShield®2545 is a polyamide 6 (nylon 6) product,. It is available in North America. OxyShield®2545 application areas include packaging and movies.

Features include:

high gloss

high strength

Главная Информация
Характеристики	Подсветка Высокая прочность
Используется	Двухосно-ориентированная пленка Упаковка
Формы	Пленка

Физический	Номинальное значение	Единица измерения	Метод испытания
Формовочная усадка			ASTM D955
Flow	1.3 - 2.0	%	ASTM D955
Transverse flow	0.0 - 0.50	%	ASTM D955

Механические	Номинальное значение	Метод испытания
Коэффициент трения		ASTM D1894
With Metal-Dynamic	0.27	ASTM D1894
With self-dynamics	0.78	ASTM D1894

Пленки	Номинальное значение	Единица измерения	Метод испытания
Толщина пленки протестирована	28	µm
Сектантный модуль			ASTM D882
MD	2840	MPa	ASTM D882
TD	2840	MPa	ASTM D882
Прочность на растяжение			ASTM D882
MD : Fracture	248	MPa	ASTM D882
TD : Fracture	248	MPa	ASTM D882
Удлинение при растяжении			ASTM D882
MD : Fracture	90	%	ASTM D882
TD : Fracture	90	%	ASTM D882
Elmendorf Tear Strength			ASTM D1922
MD	19	g	ASTM D1922
TD	19	g	ASTM D1922
Проницаемость кислорода (23°C, 65% RH)	0.21	cm³·mm/m²/atm/24 hr	ASTM D3985
Передача водяного пара	9.3	g/m²/24 hr	ASTM E96

Оптический	Номинальное значение	Единица измерения	Метод испытания
Блеск (20°)	80		ASTM D2457
Haze	5.0	%	ASTM D1003

Дополнительная информация
Tensile Strength @ Break, ASTM D 882, MD & TD: 30000 - 42000 psiElongation @ Break, ASTM 882, MD & TD: 70 - 110%Secant Modulus, ASTM D 882, MD & TD: 350000 - 475000 psiElmendorf Tear Str, ASTM D 1922, MD & TD: 15 - 19 g/milGraves Tear (initial), ASTM D 1004: 1100 - 1400 g/milGloss (20°), ASTM D 2457: 75 - 85Coefficient of Friction, ASTM D 1894: 0.65 - 0.90 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.24 - 0.30 vs Metal-DynamicOxygen Permeability, ASTM D 3985, 73°F/0% RH: .52 cc/100 in²/dayThe value listed as Mold Shrink, Linear-Flow, ASTM D 955, was tested in accordance with ASTM D 1204.The value listed as Mold Shrink, Linear-Trans, ASTM D 955, was tested in accordance with ASTM D 1204.The value listed as Water Vapor Transmission , ASTM E 96, was tested in accordance with ASTM F 1249.

Дополнительная информация

Tensile Strength @ Break, ASTM D 882, MD & TD: 30000 - 42000 psiElongation @ Break, ASTM 882, MD & TD: 70 - 110%Secant Modulus, ASTM D 882, MD & TD: 350000 - 475000 psiElmendorf Tear Str, ASTM D 1922, MD & TD: 15 - 19 g/milGraves Tear (initial), ASTM D 1004: 1100 - 1400 g/milGloss (20°), ASTM D 2457: 75 - 85Coefficient of Friction, ASTM D 1894: 0.65 - 0.90 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.24 - 0.30 vs Metal-DynamicOxygen Permeability, ASTM D 3985, 73°F/0% RH: .52 cc/100 in²/dayThe value listed as Mold Shrink, Linear-Flow, ASTM D 955, was tested in accordance with ASTM D 1204.The value listed as Mold Shrink, Linear-Trans, ASTM D 955, was tested in accordance with ASTM D 1204.The value listed as Water Vapor Transmission , ASTM E 96, was tested in accordance with ASTM F 1249.

Тип материала	Категория	Производитель
Ultramid® 8231G HS BK-106	Nylon 6	BASF Corporation
NYCOA Polyamide 446	Nylon 6	Nycoa (Nylon Corporation of America)
Cheng Yu NGC3	Nylon 6	Cheng Yu Plastic Company Limited
Electrafil® PA6 C BK	Nylon 6	Techmer Engineered Solutions
KOPLA PA6 KNE1030	Nylon 6	KOPLA Co., Ltd.
PLASTRON™ PA6-GF60-01	Nylon 6	Daicel Polymer Ltd.

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

