Описание материалов:
SABIC® LDPE 2602H0 is a grade with very good optical properties. The grade contains no additives, has an increased density and shows a very good draw down ability. The films are characterized by good mechanical properties.
Application
Blown Film: SABIC® LDPE 2602H0 is typically developed for applications where enhanced stiffness is required.
Cast Film: SABIC® LDPE 2602H0 is typically developed for applications, where enhanced stiffness is required. It is used in combination with LLDPE for e.g. diaper film or underblankets. This grade is also suitable for bubble film.
This product is not intended for and must not be used in any pharmaceutical/medical applications.
| Главная Информация | |
|---|
| Характеристики | - Низкая плотность
- Жесткий, хороший
- Оптическая производительность
- Хорошее Отшелушивание
|
| Используется | - Выдувная пленка
- Литая пленка
|
| Метод обработки | - Выдувная пленка
- Литая пленка
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.926 | g/cm³ | ISO 1183/A |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 1.9 | g/10 min | ISO 1133 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Коэффициент трения (Blown Film) | > 1.0 | | ASTM D1894 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Эластичный модуль-
MD (25 µm, Cast Film) | 140 | MPa | ASTM D882 |
| Эластичный модуль-
TD (25 µm, Cast Film) | 160 | MPa | ASTM D882 |
| Модуль растяжения | | | ISO 527-3 |
| MD
: 25 µm, blown film | 250 | MPa | ISO 527-3 |
| TD
: 25 µm, blown film | 260 | MPa | ISO 527-3 |
| Прочность на растяжение | | | |
| MD
: Yield, 25 µm, extruded film | 10.0 | MPa | ASTM D882 |
| TD
: Yield, 25 µm, extruded film | 10.0 | MPa | ASTM D882 |
| MD
: Yield, 25 µm, blown film | 13.0 | MPa | ISO 527-3 |
| TD
: Yield, 25 µm, blown film | 13.0 | MPa | ISO 527-3 |
| MD
: Broken, 25 µm, extruded film | 21.0 | MPa | ASTM D882 |
| TD
: Broken, 25 µm, extruded film | 21.0 | MPa | ASTM D882 |
| MD
: Broken, 25 µm, blown film | 30.0 | MPa | ISO 527-3 |
| TD
: Broken, 25 µm, blown film | 20.0 | MPa | ISO 527-3 |
| Удлинение при растяжении | | | |
| MD
: Broken, 25 µm, extruded film | 300 | % | ASTM D882 |
| TD
: Broken, 25 µm, extruded film | 350 | % | ASTM D882 |
| MD
: Broken, 25 µm, blown film | > 200 | % | ISO 527-3 |
| TD
: Broken, 25 µm, blown film | > 500 | % | ISO 527-3 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Impact Strength | | | ASTM D4272 |
| Blown Film
: 25.0 µm | 150 | J/cm | ASTM D4272 |
| Cast Film
: 25.0 µm | 130 | J/cm | ASTM D4272 |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блокировка-
Выдувная пленка
(25,0 мкм) | 10 | g | Internal method |
| Повторная Блокировка-
Выдувная пленка
(25,0 мкм) | 30 | g | Internal method |
| Tear Strength 1 | | | ISO 6383-2 |
| MD
: 25.0 µm | 90.0 | kN/m | ISO 6383-2 |
| TD
: 25.0 µm | 40.0 | kN/m | ISO 6383-2 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Викат Температура размягчения | 99.0 | °C | ISO 306/A |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блеск | | | ASTM D2457 |
| 45, 25.0 µm, blown film | 64 | | ASTM D2457 |
| 45, 25.0 µm, cast film | 86 | | ASTM D2457 |
| Haze | | | ASTM D1003 |
| 25.0 µm, blown film | 7.0 | % | ASTM D1003 |
| 25.0 µm, cast film | 1.5 | % | ASTM D1003 |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Blown FilmFilm properties have been measured at film of 25 µm with a BUR of 3.The film has been produced on Kiefel IBC blown film line with 200 kg/h. Die size 200 mm, die gap 0.8 mm.Cast FilmThe optical and film properties are determined on 25 µm cast film. Die gap 1.0 mm. |