Описание материалов:
Bayfill 369 is a semi-rigid polyurethane foam system designed for automotive interior applications. The Bayfill 369 system is an excellent choice for the production of soft-touch panels, such as instrument panels, door trim, and center consoles. The foam is typically molded in a back-filling process between a soft, exterior skin and a rigid, thermoplastic substrate.
The Bayfill 369 system is supplied as two components. Component A is a polymeric diphenylmethane diisocyanate (PMDI). Component B is a polyol mixture. As with any product, use of the Bayfill 369 system in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Используется | - Пена
- Применение в автомобильной области
- Автомобильные внутренние детали
- Оборудование для салона автомобиля
- Приборная панель автомобиля
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Литая плотность | 147 | kg/m³ | ASTM D3574A |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Отклонение силы сжатия | | | ASTM D3574C |
| -- 1 | 0.0689 | MPa | ASTM D3574C |
| -- 2 | 0.0207 | MPa | ASTM D3574C |
| Комплект сжатия | | | ASTM D3574D |
| Cd 3 | 66 | % | ASTM D3574D |
| Cd 4 | 33 | % | ASTM D3574D |
| Ct 5 | 16 | % | ASTM D3574D |
| Ct 6 | 33 | % | ASTM D3574D |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение | | | |
| -- 7 | 0.0965 | MPa | ASTM D3574K |
| -- | 0.241 | MPa | ASTM D3574E |
| Удлинение при растяжении | | | |
| Fracture 8 | 46 | % | ASTM D3574K |
| Fracture | 61 | % | ASTM D3574E |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tear Strength | 0.123 | kN/m | ASTM D3574F |
| Термокомплект | Номинальное значение | | |
|---|
| Компоненты термокомплекта | | | |
| Component a | Mixing ratio by weight: 42 | | |
| Component B | Mixing ratio by weight: 100 | | |
| Дополнительная информация |
|---|
| Part A
Type: Isocyanate
Appearance: Dark brown liquid
Specific Gravity @ 25°C: 1.24
Viscosity @25°C: 60 cps
Flash Point PMCC: 149°C
NCO: 32.2 wt%
Part B
Type: Polyol
Appearance: Colorless to light tan viscous liquid
Specific Gravity @ 25°C: 1.03
Viscosity @25°C: 1100 cps
Flash Point PMCC: 117°C
Water: 2 wt%
Hydroxyl Number: 70 KOH/g
Mold Temperature: 38 to 43°CDemold Time: >90 secHand Mix Reactivity at 25°C
Cream Time: 9 to 17 sec
Top of Cup Time: 36 to 50 sec
Gel Time: 39 to 53 to sec
Rise Time: 67 to 83 sec
Free-Rise Density: 4.90 to 5.70 lb/ft³
Machine Reactivity at 27 to 32°C
Cream Time: 6 to 10 sec
Top of Cup Time: 20 to 22 sec
Gel Time: 27 to 31 sec
Rise Time: 44 to 48 sec
Free-Rise Density: 4.00 to 5.00 lb/ft³
Molded Density: 7 to 10.5 lb/ft³ |
| Примечание |
|---|
| 1 . | 0.5 |
| 2 . | After J2 Autoclave |
| 3 . | After J2 Autoclave, Cd=compression set as a percentage of the original deflection |
| 4 . | 50, Cd=compression set as a percentage of the original deflection |
| 5 . | 50%, Ct=compression set as a percentage of the original thickness |
| 6 . | After J2 Autoclave, Ct=compression set as a percentage of the original thickness |
| 7 . | Dry Heat Aged at 140°C |
| 8 . | Dry Heat Aged at 140°C |