TOPAS® 8007F-04
| Категория | COC, Cyclic Olefin Copolymer |
| Производитель | Topas Advanced Polymers, Inc. |
| Торговая марка | TOPAS® |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
OgS3kT_TOPAS-8007F-04.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Product Description
TOPAS 8007F-04 is a general purpose film extrusion grade. It is a high clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and healthcare applications. It is used in monolayer cast applications, and in coextrusions in both cast and blown processes, for a wide variety of film and sheet products requiring excellent optics in applications such as blister, twist, barrier, shrink and easy tear packaging. Industrial uses include formed decorative sheet products. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended.
Selected Applications
Leading Attributes
Related Grades for Packaging and Film Extrusion
TOPAS 8007F-04 is a general purpose film extrusion grade. It is a high clarity amorphous resin with high stiffness, moisture barrier, chemical resistance, thermoformability and purity for food and healthcare applications. It is used in monolayer cast applications, and in coextrusions in both cast and blown processes, for a wide variety of film and sheet products requiring excellent optics in applications such as blister, twist, barrier, shrink and easy tear packaging. Industrial uses include formed decorative sheet products. For property enhancement at elevated temperatures, higher glass transition temperature (Tg) grades of TOPAS are recommended.
Selected Applications
- Pharmaceutical blisters
- Deep draw barrier trays
- Shrink films and labels
- Twist films
- Decorative sheet
- Food packaging
- Healthcare and food contact
Leading Attributes
- Clarity, forming, barrier, purity, halogen-free
- Excellent deep forming, unlike other barriers
- High shrink, low stress, gloss, clarity, toughness
- High gloss, outstanding deadfold, clean cutting
- Gloss, hardness, chemical resistance, forming
- Not manufactured with BPA, phthalates, or halogens
- Broad regulatory compliance
Related Grades for Packaging and Film Extrusion
- TOPAS 8007F-400 - robust extrusion grade especially for PE blends
- TOPAS 8007F-600 - robust clarity extrusion grade especially for PE blends
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 1.02 | g/cm³ | ISO 1183 |
| Массовый расход расплава (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 1.8 | g/10 min | ISO 1133 |
| 230°C/2.16 kg | 11 | g/10 min | ISO 1133 |
| Плавкий объем-расход (MVR) | ISO 1133 | ||
| 190°C/2.16 kg | 2.00 | cm³/10min | ISO 1133 |
| 230°C/2.16 kg | 12.0 | cm³/10min | ISO 1133 |
| Поглощение воды (Saturation, 23°C) | 0.010 | % | ISO 62 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 70 | µm | |
| Модуль растяжения | ISO 527-3/1 | ||
| MD : 70 µm, cast film | 2200 | MPa | ISO 527-3/1 |
| TD : 70 µm, cast film | 1800 | MPa | ISO 527-3/1 |
| Tensile Stress | ISO 527-3/50 | ||
| MD : Fracture, 70 µm, cast film | 57.0 | MPa | ISO 527-3/50 |
| TD : Fracture, 70 µm, cast film | 50.0 | MPa | ISO 527-3/50 |
| Удлинение при растяжении | ISO 527-3/50 | ||
| MD : Fracture, 70 µm, cast film | 2.9 | % | ISO 527-3/50 |
| TD : Fracture, 70 µm, cast film | 3.0 | % | ISO 527-3/50 |
| Ударное падение Dart (70 µm, cast film) | < 36 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 70 µm, cast film | 2.2 | N | ISO 6383-2 |
| TD : 70 µm, cast film | 2.3 | N | ISO 6383-2 |
| Проницаемость кислорода (23°C, 70 µm, extruded film, 50% RH) | 25 | cm³·mm/m²/atm/24 hr | ASTM D3985 |
| Скорость передачи водяного пара (70 µm, 23°C, Cast Film, 85% RH) | 0.094 | g·mm/m²/atm/24 hr | ASTM F1249 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Температура перехода стекла | 78.0 | °C | ISO 11357-2 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (60, 70.0 µm, cast film) | > 100 | ISO 2813 | |
| Haze (70.0 µm, cast film) | < 1.0 | % | ISO 14782 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Кормовая часть экструдера | 20 - 60 | °C | |
| Экструдер винт L/D Соотношение | > 28:1 | ||
| Зона цилиндра 1 темп. | 210 - 220 | °C | |
| Зона цилиндра 2 температура. | 230 - 240 | °C | |
| Зона цилиндра 3 темп. | 230 - 240 | °C | |
| Зона цилиндра 4 темп. | 230 - 240 | °C | |
| Температура матрицы | 230 - 240 | °C |
| Инструкции по экструзии |
|---|
| Head pressure: P > 140 bar / 2000 psi; Fine screen packs as neededScrew speed: RPM > 50% nominalScrew design: Multi-purpose or barrier screw with mixing section Screw diameter > 60 mm / 2.5 inch Grooved Feed: Hot temperature: 120°C (248°F) |
| Тип материала | Категория | Производитель |
|---|---|---|
| TOPAS® 6013EC-01 | COC | Polyplastics Co., Ltd. |
| TOPAS® 9506F-500 | COC | Polyplastics Co., Ltd. |
| APEL™ APL5014DP | COC | Mitsui Chemicals America, Inc. |
| TOPAS® 6013M-07 | COC | Topas Advanced Polymers, Inc. |
| TOPAS® 8007X-10 | COC | Topas Advanced Polymers, Inc. |
| APEL™ APL5014CL | COC | Mitsui Chemicals, Inc. |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved