Visico™ LE4427/Ambicat™ LE4476
| Категория | XLPE, Crosslinked Polyethylene |
| Производитель | Borealis AG |
| Торговая марка | Visico™ |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
OWwMoe_Visico-LE4427-Ambicat-LE4476.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Visico LE4427 / Ambicat LE4476 is a silane crosslinkable natural compound designed for weather resistant covering/insulation of overhead and façade cables.
The black base material Visico LE4427 in combination with the catalyst masterbatch Ambicat LE4476 will accelerate the moisture-induced crosslinking reaction. The system is highly active and crosslinks quickly at ambient conditions, in sauna or in hot water.
When properly mixed, addition of 5 parts of Ambicat LE4476 to 95 parts of Visico LE4427 , insulation with excellent thermo-oxidative stability, also in contact with copper as well as aluminium, is achieved.
Visico LE4427 / Ambicat LE4476 contains antioxidant, metal deactivator and a drying agent. Visico LE4427 contains a permanent scorch retardant additive, ensuring safe processing and enabling the use of highly active crosslinking catalyst.
Visico LE4427 / Ambicat LE4476 in combination meets the applicable requirements as below when processed using sound extrusion and testing procedure:
The standards referred to above is a selection and is not complete coverage of all applicable standards. Contact your Borealis representative for additional information.
The black base material Visico LE4427 in combination with the catalyst masterbatch Ambicat LE4476 is a readymade two-component system which crosslinks quickly at ambient conditions, in sauna or in hot water. The base material Visico LE4427 is a black filled low density polyethylene, copolymerised with vinyl silane and designed for overhead cable covering/insulation. Visico LE4427 contains a well dispersed carbon black to provide the necessary protection for outdoor weatherability according to the French specification NF C 33 209 part 6-2, Cable de Façade. The catalyst masterbatch, Ambicat LE4476 , contains a novel, patented, environmentally friendly crosslinking catalyst and is completely free from heavy metals.
The black base material Visico LE4427 in combination with the catalyst masterbatch Ambicat LE4476 will accelerate the moisture-induced crosslinking reaction. The system is highly active and crosslinks quickly at ambient conditions, in sauna or in hot water.
When properly mixed, addition of 5 parts of Ambicat LE4476 to 95 parts of Visico LE4427 , insulation with excellent thermo-oxidative stability, also in contact with copper as well as aluminium, is achieved.
Visico LE4427 / Ambicat LE4476 contains antioxidant, metal deactivator and a drying agent. Visico LE4427 contains a permanent scorch retardant additive, ensuring safe processing and enabling the use of highly active crosslinking catalyst.
Visico LE4427 / Ambicat LE4476 in combination meets the applicable requirements as below when processed using sound extrusion and testing procedure:
- ANSI/ICEA S-70-547
- ASTM D 1248 Type II, Class C, Category 4
- HD 603 S1
- HD 626 S1 (TIX-2, TIX-3, TIX-5, TIX-7, TIX8)
- NF C33-209 part 6-2 (Except messenger wire)
- NEMA WC 70
- NEMA WC 71
The standards referred to above is a selection and is not complete coverage of all applicable standards. Contact your Borealis representative for additional information.
The black base material Visico LE4427 in combination with the catalyst masterbatch Ambicat LE4476 is a readymade two-component system which crosslinks quickly at ambient conditions, in sauna or in hot water. The base material Visico LE4427 is a black filled low density polyethylene, copolymerised with vinyl silane and designed for overhead cable covering/insulation. Visico LE4427 contains a well dispersed carbon black to provide the necessary protection for outdoor weatherability according to the French specification NF C 33 209 part 6-2, Cable de Façade. The catalyst masterbatch, Ambicat LE4476 , contains a novel, patented, environmentally friendly crosslinking catalyst and is completely free from heavy metals.
| Главная Информация | |
|---|---|
| Добавка |
|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Внешний вид |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность 1 | 0.935 | g/cm³ | ISO 1183 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ISO 1133 |
| Экологическое сопротивление растрескиванию (Condition B, 50°C, 10% Igepal, F20) | > 96.0 | hr | IEC 60811-4-1/B |
| Содержание черного углерода | 2.5 | % | ISO 6964 |
| Старение | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Изменение растяжимых свойств- 240 h (150 °C) | < 25 | % | IEC 60811-1-2 |
| Сохранение растяжимых свойств | |||
| -- 2 | > 85 | % | |
| -- 3 | > 70 | % |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Горячий набор | IEC 60811-2-1 | ||
| 200°C 4 | 30 | % | |
| 200°C 5 | 0.0 | % |
| Дополнительная информация | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Crosslinking | |||
| 700.0 µm 6 | 2.0 | day | |
| 700.0 µm 7 | < 25.0 | min | |
| 1.80 mm 8 | 1.00 | hr | |
| 1.80 mm 9 | 7.0 | day |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Tensile Stress (Yield) | > 15.0 | MPa | ISO 527-2/250 |
| Растяжимое напряжение (Break) | > 300 | % | ISO 527-2/250 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Температура ломкости | < -76.0 | °C | ASTM D746 |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Сопротивление громкости | 1.0E+15 | ohms·cm | IEC 60093 |
| Диэлектрическая постоянная (50 Hz) | < 2.90 | IEC 60250 | |
| Коэффициент рассеивания (50 Hz) | < 1.0E-3 | IEC 60250 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Зона цилиндра 1 темп. | 150 | °C | |
| Зона цилиндра 2 температура. | 170 | °C | |
| Зона цилиндра 3 темп. | 170 | °C | |
| Зона цилиндра 4 темп. | 170 | °C | |
| Температура матрицы | 170 | °C |
| Примечание | |
|---|---|
| 1 . | Mixture 93:7, ISO 1872-2 |
| 2 . | After UV Ageing, 3 to 6 weeks |
| 3 . | After UV Ageing, 6 weeks |
| 4 . | Elongation under load, 0.20 MPa |
| 5 . | Permanent deformation, 0.20 MPa |
| 6 . | In air 23°C, 50 % humidity |
| 7 . | 90°C, Sauna or water bath |
| 8 . | 90°C, Sauna or water bath |
| 9 . | In air 23°C, 50 % humidity |
| Тип материала | Категория | Производитель |
|---|---|---|
| Syncure™ System S117FH | XLPE | PolyOne Corporation |
| Syncure™ V0064G RoHS | XLPE | PolyOne Corporation |
| Syncure™ S1042A Natural | XLPE | PolyOne Corporation |
| GETILAN GPE/452 BLACK | XLPE | Crosspolimeri S.p.A. |
| SCHULINK® XL 350-S | XLPE | A. Schulman Inc. |
| Visico™ LE4421/Ambicat™ LE4472 | XLPE | Borealis AG |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved