AVIMID® RB is a high temperature, 644°F (340°C) Tg thermoset polyimide resin with wet service capability to more than 530°F (277°C) and dry service capability of 600°F (316°C). AVIMID RB has excellent thermal oxidative stability and resistance to aircraft fluids.
AVIMID RB was formulated for prepreg autoclave vacuum bag processing, but can be successfully compression molded both as a prepreg and in dry forms as neat resin or chopped-fiber molding compound. Unidirectional tape and woven prepreg of AVIMID RB will retain their tack and drape for 14 days at 70°F (21°C).
Standard autoclave or compression molding processes, to a final temperature of 680°F (360°C) will result in full Tg development/cure with no need for post-cure treatment. AVIMID RB can be solution impregnated on a variety of fibers and fabrics.
| Главная Информация | |
|---|
| Характеристики | - Автоклавный
- Хорошая термостойкость к старению
- Термическое лечение
- Высокая термостойкость
- Устойчивость к окислению
|
| Используется | - Аэрокосмическое применение
- Детали конструкции
|
| Формы | |
| Метод обработки | - Прессформа сжатия
- Вакуумная формовка
|
| Механические | Номинальное значение | Единица измерения | |
|---|
| Модуль растяжения 1 | 3790 | MPa | |
| Прочность на растяжение 2 | 82.7 | MPa | |
| Удлинение при растяжении (Break) | 2.4 | % | |
| Флекторный модуль | 3790 | MPa | |
| Flexural Strength | 111 | MPa | |
| Примечание |
|---|
| 1 . | Neat resin |
| 2 . | Neat resin |