Описание материалов:
Durastar™ DS1010 polymer contains a mold release. It has excellent appearance and clarity. Its most outstanding features are chemical resistance and excellent processing characteristics. Exposure to aromatic oils often causes crazing or actual fracture of many polymer resins, but DS1010 maintains its physical properties when exposed to these oils, and its appearance is virtually unchanged. Easy to process, it flows readily, fills intricate molds, and is well suited for thick-wall applications. Under existing United States Food and Drug Administration (FDA) regulations, Durastar™ DS1010 may be used in food contact articles which comply with the specifications and conditions of use in 21 CFR 177.1240. This product is certified to ANSI/NSF Standard 51.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Цикл быстрого формования
- Приемлемый пищевой контакт
- Хорошая химическая стойкость
- Хороший поток
- Хорошая ударопрочность
- Хороший выпуск пресс-формы
- Хорошая технологичность
- Высокая четкость
- Приятный внешний вид
|
| Используется | - Компоненты прибора
- Приборы
- Обслуживание/ремонт напольных покрытий
- Мебель
- Товары для дома
- Спортивные товары
- Толстостенные детали
- Игрушки
- Инструменты для письма
|
| Рейтинг агентства | - Управление по санитарному надзору за качеством пищевых продуктов и медикаментов 21 CFR 177,1240
- Утверждено NSF 51
|
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | | | |
| -- | 1.20 | g/cm³ | ASTM D792 |
| 23°C | 1.19 | g/cm³ | ISO 1183 |
| Формовочная усадка-
Поток (3.20 mm) | 0.20 to 0.60 | % | ASTM D955 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale, 23°C) | 103 | | ASTM D785 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения (23°C) | 1800 | MPa | ISO 527-2 |
| Прочность на растяжение | | | |
| Yield, 23°C | 47.0 | MPa | ASTM D638, ISO 527-2 |
| Break, 23°C | 51.0 | MPa | ASTM D638 |
| Break, 23°C | 46.0 | MPa | ISO 527-2 |
| Удлинение при растяжении | | | |
| Yield, 23°C | 5.0 | % | ASTM D638 |
| Yield, 23°C | 4.0 | % | ISO 527-2 |
| Break, 23°C | 300 | % | ASTM D638 |
| Break, 23°C | 200 | % | ISO 527-2 |
| Флекторный модуль | | | |
| 23°C | 2000 | MPa | ASTM D790 |
| 23°C | 1850 | MPa | ISO 178 |
| Флекторный стресс | | | |
| 23°C | 65.0 | MPa | ISO 178 |
| Yield, 23°C | 69.0 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | | | |
| -40°C | 40 | J/m | ASTM D256 |
| 23°C | 80 | J/m | ASTM D256 |
| -40°C | 4.8 | kJ/m² | ISO 180 |
| 23°C | 7.8 | kJ/m² | ISO 180 |
| Незубчатый изод Impact | | | ASTM D4812 |
| -40°C | No Break | | |
| 23°C | No Break | | |
| Ударное устройство для дротиков | | | |
| -40°C, Energy at Peak Load | 48.0 | J | ASTM D3763 |
| 23°C, Energy at Peak Load | 42.0 | J | ASTM D3763 |
| -40°C, Energy to Peak Force | 52.6 | J | ISO 6603-2 |
| 23°C, Energy to Peak Force | 58.7 | J | ISO 6603-2 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | |
| 0.45 MPa, Unannealed | 75.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 72.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 66.0 | °C | ISO 75-2/A |
| Воспламеняемость | Номинальное значение | | Метод испытания |
|---|
| Огнестойкость (3.00 mm, AT) | V-2 | | UL 94 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Коэффициент пропускания | | | ASTM D1003 |
| Total | 91.0 | % | |
| Regular | 89.0 | % | |
| Haze | 0.30 | % | ASTM D1003 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 71.0 | °C | |
| Время сушки | 3.0 to 4.0 | hr | |
| Температура обработки (расплава) | 232 to 277 | °C | |
| Температура формы | 16.0 to 38.0 | °C | |