Permanently antistatic and electrically conductive polyamide 12 compounds
Characterization: high viscosity, heat- and light-stabilized, increased cold impact strength, with processing aid
Application Examples: antistatic and electrically conductive moldings or extrudates for use in areas prone to explosion such as coal mining and other industries, e.g., housings for explosion-protected measurement equipment and switches, ventilation fans for electric motors, chair castors, loud speaker boxes, telephone and radio equipment, profiles for assembly lines, also with electric shock protection
The properties of PA 12 compounds can be modified to suit the requirements of many applications by incorporating various additives such as stabilizers, plasticizers, reinforcements, and fillers.
The VESTAMID® L compounds of Evonik comprise a range of various products that are customized to the requirements of processors and users. Many of the PA 12 compounds are suitable especially for the injection molding of recision parts; others have been developed specifically for the extrusion process.
| Главная Информация | |
|---|
| Добавка | - Стабилизатор тепла
- Обработка помощи
- UV Stabilizer
|
| Характеристики | - Антистатический
- Электропроводящий
- Устойчивость к усталости
- Приемлемый пищевой контакт
- Топливная устойчивость
- Хорошая стойкость к истиранию
- Хорошая ударопрочность
- Хорошая технологичность
- Устойчивость к смазке
- Стабилизация тепла
- Высокий уровень ЭСКП (устойчивость к стрессу)
- Высокая вязкость
- Стабилизированный свет
- Низкое поглощение воды
- Маслостойкий
- Устойчивость к растворителям
- Демпфирование звука
- Вибрационное Демпфирование
|
| Используется | - Электрическое/электронное применение
- Корпуса
- Приложения для горнодобывающей промышленности
- Профили
|
| Рейтинг агентства | |
| Внешний вид | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность (23°C) | 1.06 | g/cm³ | ISO 1183 |
| Формовочная усадка | | | ISO 294-4 |
| Across Flow | 1.6 | % | |
| Flow | 1.6 | % | |
| Поглощение воды | | | ISO 62 |
| Saturation, 23°C | 1.2 | % | |
| Equilibrium, 23°C, 50% RH | 0.50 | % | |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 1500 | MPa | ISO 527-2 |
| Tensile Stress | | | ISO 527-2 |
| Yield | 42.0 | MPa | |
| Break | 36.0 | MPa | |
| Растяжимое напряжение | | | ISO 527-2 |
| Yield | 9.0 | % | |
| Break | 44 | % | |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность | | | ISO 179/1eA |
| -30°C, Complete Break | 9.0 | kJ/m² | |
| 23°C, Complete Break | 21 | kJ/m² | |
| Charpy Unnotched Impact Strength | | | ISO 179/1eU |
| -30°C | No Break | | |
| 23°C | No Break | | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature | | | |
| 0.45 MPa, Unannealed | 130 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | °C | ISO 75-2/A |
| Викат Температура размягчения | | | |
| -- | 175 | °C | ISO 306/A |
| -- | 140 | °C | ISO 306/B |
| Температура плавления 1 | 178 | °C | ISO 11357-3 |
| CLTE-
Поток (23 to 55°C) | 1.5E-4 | cm/cm/°C | ISO 11359-2 |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Сопротивление громкости | 1.0E+3 | ohms·cm | IEC 60093 |
| Insulation Resistance | 1.0E+3 | ohms | IEC 60167 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость | | | UL 94 |
| 1.60 mm | HB | | |
| 3.20 mm | HB | | |
| Дополнительная информация | Номинальное значение | | Метод испытания |
|---|
| ISO Shortname | PA12-HI, EHZ, 22-010 | | ISO 1874 |