MAGNUM™ 275

Категория ABS, ABS Resin
Производитель Trinseo
Торговая марка MAGNUM™
Порт Китай Шанхайский порт
Торговые условия FOB, CFR, CIF
Платежное средство L/C, T/T, Western Union
PDF NATOM0_MAGNUM-275.pdf
Контактная информация
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Описание материалов:
MAGNUM™ 275 ABS resin is a low gloss, low flow ABS resin with good impact. MAGNUM ABS resins are thermoplastic materials that provide an excellent balance of processability, impact resistance, and heat resistance as imparted by the various polymer compositions. MAGNUM ABS resins are available in a wide range of melt flow rates, impact strengths, and heat resistances for both high and low gloss applications manufactured by injection molding, sheet or profile extrusion, and thermoforming. MAGNUM ABS resins offer a wide range of processing abilities and impact resistance for low gloss injection molding applications. Combined with heat resistance, tensile and flexural strength, MAGNUM ABS resins are used in a wide variety of injection molding applications.

Applications
  • Injection molding applications
  • Extrusion and thermoforming applications

Complies with:
  • U.S. FDA 21 CFR 181.32
Consult the regulations for complete details.
Главная Информация
Характеристики
  • Хорошая ударопрочность
  • Хорошая технологичность
  • Высокая термостойкость
  • Низкий поток
  • Низкий блеск
Рейтинг агентства
  • Управление по санитарному надзору за качеством пищевых продуктов и медикаментов 21 CFR 181,32
Формы
  • Гранулы
Метод обработки
  • Экструзия
  • Литье под давлением
  • Термоформовка
ФизическийНоминальное значениеЕдиница измеренияМетод испытания
Удельный вес
    -- 1.04g/cm³ASTM D792
    -- 1050kg/m³ISO 1183 1
Массовый расход расплава (MFR) (230°C/3.8 kg)2.6g/10 minASTM D1238
Плавкий объем-расход (220°C/10.0 kg)9.00cm³/10minISO 1133 2
Формовочная усадка- Поток 0.40 to 0.70%ASTM D955
МеханическиеНоминальное значениеЕдиница измеренияМетод испытания
Модуль растяжения
    -- 31830MPaASTM D638
    -- 2000MPaISO 527-2 4
Прочность на растяжение
    Yield 537.2MPaASTM D638
    Yield 44.0MPaISO 527-2 6
    Break 734.5MPaASTM D638
Удлинение при растяжении
    Yield 83.0%ASTM D638
    Yield 2.6%ISO 527-2 9
    Break 10100%ASTM D638
Номинальное напряжение при разрыве 30%ISO 527-2 11
Флекторный модуль 122030MPaASTM D790
Flexural Strength 1363.4MPaASTM D790
ВоздействиеНоминальное значениеЕдиница измеренияМетод испытания
Ударная прочность ISO 179/1eA 14
    -30°C 9.00kJ/m²
    23°C 22.0kJ/m²
Ударная сила Шарпи ISO 179/1eU 15
    -30°C No Break
    23°C No Break
Зубчатый изод Impact 16ASTM D256
    -18°C, 3.20 mm 130J/m
    23°C, 3.20 mm 270J/m
Ударное устройство для дротиков ASTM D3763
    -18°C, Peak Energy 32.8J
    -18°C, 3.20 mm, Total Energy 1737.3J
    23°C, Peak Energy 32.8J
    23°C, 3.20 mm, Total Energy 1846.3J
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Температура отклонения при нагрузке
    0.45 MPa, Unannealed, 3.20 mm 93.3°CASTM D648
    0.45 MPa 95.0°CISO 75-2 19
    1.8 MPa, Unannealed, 3.20 mm 79.4°CASTM D648
    1.8 MPa 85.0°CISO 75-2 20
Викат Температура размягчения
    -- 107°CASTM D1525
    50°C/h, B (50N) 99.0°CISO 306 21
CLTE- Поток 7.9E-5cm/cm/°CISO 11359-2 22
ВоспламеняемостьНоминальное значениеМетод испытания
Огнестойкость 23(1.52 mm)HBUL 94
Горение beadv. at 1,6 мм nom. Толстый. (1.47 mm, UL)HBISO 1210 24
Примечание
1 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
2 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
3 .1000 mm/min
4 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
5 .Type I, 51 mm/min
6 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
7 .Type I, 51 mm/min
8 .Type I, 51 mm/min
9 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
10 .Type I, 51 mm/min
11 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
12 .Type I, 2000 mm/min
13 .Type I, 2000 mm/min
14 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
15 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
16 .0.25 mm Notch Depth
17 .3.39 m/sec
18 .3.39 m/sec
19 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
20 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
21 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
22 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
23 .This rating not intended to reflect hazards presented by this or any other material under actual fire conditions.
24 .Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted.
Тип материала Категория Производитель
Shuman ABS 730 ABS Shuman Plastics, Inc.
TES J-1200/10/V0/ND BK2089 ABS Techmer Engineered Solutions
Abstron IM29 ABS Bhansali Engineering Polymers Limited
Absolac® 150 ABS Styrolution
LNP™ LUBRICOMP™ AI001XXH compound ABS SABIC Innovative Plastics
LNP™ STAT-KON™ AE002 compound ABS SABIC Innovative Plastics
Получите информацию об этом продукте следующим способом.
Телефон+086 13424755533
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат