Edgetek™ ET6620-0020 FRV0
Описание материалов:
The Edgetek® Engineering Thermoplastic Compounds portfolio covers a broad range of standard and custom-formulated high performance materials. This portfolio includes high-temperature materials for elevated service temperature environments, high-modulus / structural materials for load-bearing and high-strength applications and flame-retardant products. These compounds are based on select engineering thermoplastic resins that are compounded with reinforcing additives such as carbon fiber, glass fiber and glass beads.
| Главная Информация | |
|---|
| Характеристики | |
| Номер файла UL | |
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.50 | g/cm³ | ASTM D792 |
| Формовочная усадка-
Поток | 0.30 | % | ASTM D955 |
| Поглощение воды (23°C, 24 hr) | 0.30 | % | Internal Method |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 8270 | MPa | ASTM D638 |
| Прочность на растяжение | 117 | MPa | ASTM D638 |
| Удлинение при растяжении (Break) | 2.0 | % | ASTM D638 |
| Флекторный модуль | 7580 | MPa | ASTM D790 |
| Flexural Strength | 159 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | 35 | J/m | ASTM D256 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке (1.8 MPa, Unannealed, 3.18 mm) | 187 | °C | ASTM D648 |
| Воспламеняемость | Номинальное значение | | Метод испытания |
|---|
| Огнестойкость | | | UL 94 |
| 1.59 mm | V-0 | | |
| 3.18 mm | V-0 | | |