Описание материалов:
Menzolit® BMC 1650 is a bulk moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is injection moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens nor any heavy metals.
Menzolit® BMC 1650 is a specially designed anti-microbial polyester moulding compound which incorporates a "germ killer". It has been tested and found to be compliant for resistance to fungal defacement in accordance with the Standard test method BS EN ISO 846:1997. "Plastics - Evaluation of the Action of Microorganisms", and for resistance to bacterial defacement in accordance with the Standard test method "JIS Z 2801:2000. "Antimicrobial products - Test for antimicrobial activity and efficacy".AP61. Specific applications are parts within health care or sanitary equipment or furnituresThe glass content is on a level that combines good mould ability with good strength and stiffness properties. The compound is available in a varity of sanitary colours, for availability please contact your local menzolit team.
Главная Информация | |
---|
Наполнитель/армирование | - Стекловолокно, 20% наполнитель по весу
- Минеральный
|
Добавка | |
Характеристики | - Хорошая плавность
- Хорошая жесткость
- Хорошая прочность
- Без галогенов
- Низкий уровень дыма
|
Рейтинг агентства | |
Внешний вид | |
Метод обработки | |
Физический | Номинальное значение | Единица измерения | Метод испытания |
---|
Плотность | 1.90 | g/cm³ | ISO 1183 |
Формовочная усадка | | | |
-- | 0.080 | % | ISO 2577 |
-- 1 | 0.0 | % | DIN 53464 |
Поглощение воды (Saturation, 23°C) | < 0.50 | % | ISO 62 |
Механические | Номинальное значение | Единица измерения | Метод испытания |
---|
Модуль растяжения | 13000 | MPa | ISO 527-4 |
Tensile Stress (Break) | 31.0 | MPa | ISO 527-4 |
Флекторный модуль | 10000 | MPa | ISO 14125 |
Флекторный стресс | 101 | MPa | ISO 14125 |
Воздействие | Номинальное значение | Единица измерения | Метод испытания |
---|
Charpy Unnotched Impact Strength | 29 | kJ/m² | ISO 179 |
Тепловой | Номинальное значение | Единица измерения | Метод испытания |
---|
Heat Deflection Temperature (1.8 MPa, Unannealed) | > 150 | °C | ISO 75-2/A |
Температура непрерывного использования | 165 | °C | |
Температура перехода стекла | 170 | °C | ISO 11357-2 |
CLTE-
Поток | 1.0E-5 | cm/cm/°C | ISO 11359-2 |
Электрический | Номинальное значение | Единица измерения | Метод испытания |
---|
Удельное сопротивление поверхности | 1.0E+12 | ohms | IEC 60093 |
Сопротивление громкости | 1.0E+15 | ohms·cm | IEC 60093 |
Comparative Tracking Index | 600 | V | IEC 60112 |
Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
---|
Огнестойкость (3.00 mm) | HB | | UL 94 |
Температура зажигания провода свечения | 750 | °C | IEC 60695-2-13 |
Индекс кислорода | 22 | % | ISO 4589-2 |
Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
---|
Содержание волокна | 20 | % | ISO 1172 |
Glow Bar | BH2<=95 | | IEC 60707-3 |
Обозначение материала | >UP-(MD+GF)73< | | EN 14598-1 |
Инъекция | Номинальное значение | Единица измерения | |
---|
Температура формы | 135 to 150 | °C | |
Давление впрыска | 2.00 to 8.00 | MPa | |
Примечание |
---|
1 . | Post Molding Shrinkage |
Тип материала |
Категория |
Производитель |
BMC 851 |
Polyester, TS |
Bulk Molding Compounds, Inc.
|
KYOCERA TCG5910 |
TS, Unspecified |
KYOCERA Chemical Corporation
|
BMC 900 |
Polyester, TS |
Bulk Molding Compounds, Inc.
|
En Chuan 6133WAL |
Polyester, TS |
En Chuan Chemical Industries Co,. Ltd.
|
Premi-Glas® 2200-15 CR-SX |
TS, Unspecified |
Premix, Inc.
|
Glastic® 1423 |
Polyester, TS |
Bulk Molding Compounds, Inc.
|