Описание материалов:
Baytec MS-242 is a modified diphenylmethane diisocyanate (MDI)-terminated polyester prepolymer. It is used in the manufacture of high-property solid cast polyurethane elastomers, such as forklift tires, sheet goods, wheels, rollers, and seals. As with any product, use of Baytec MS-242 prepolymer in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Используется | - Колесо
- Ролик
- Уплотнение
- Лист
|
| Формы | |
| Твердость | Номинальное значение | | Метод испытания |
|---|
| Твердость дюрометра (Shore A) | 85 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Устойчивость к истиранию (1000 Cycles, 1000 g, H-18 Wheel) | 30.0 | mg | ASTM D4060 |
| Отклонение сжатия | | | ASTM D575 |
| 10% | 2.07 | MPa | ASTM D575 |
| 15% | 3.03 | MPa | ASTM D575 |
| 2% | 0.552 | MPa | ASTM D575 |
| 20% | 4.07 | MPa | ASTM D575 |
| 25% | 5.10 | MPa | ASTM D575 |
| 5% | 1.17 | MPa | ASTM D575 |
| 50% | 14.5 | MPa | ASTM D575 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ASTM D412 |
| 100% strain | 5.72 | MPa | ASTM D412 |
| 200% strain | 8.38 | MPa | ASTM D412 |
| 300% strain | 12.1 | MPa | ASTM D412 |
| Прочность на растяжение (Break) | 49.3 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 580 | % | ASTM D412 |
| Tear Strength | | | |
| -- 1 | 91.9 | kN/m | ASTM D624 |
| Cracking | 53 | kN/m | ASTM D1938 |
| Комплект сжатия (70°C, 22 hr) | 24 | % | ASTM D395 |
| Сопротивляемость Bayshore | 32 | % | ASTM D2632 |
| Дополнительная информация |
|---|
| Appearance: Light yellow solidNCO: 6.45 to 6.74 wt%Flash Point, PMCC: 260°CSpecific Gravity at 80°C: 1.18Specific Gravity at 100°C: 1.17Viscosity at 80°C: 1460 mPa-sViscosity at 100°C: 600 mPa-sNCO/OH Ratio: 1.05Stoichiometry: 95% TheoryPrepolymer Temperature: 90 to 100°CExtender Temperature: 25 to 70°CMold Temperature: 90 to 110°CPot Life: 3 to 7 minDemold: 45 to 90 min |