OnForce™ LFT LF0100-5004 X2 BLACK
Описание материалов:
PolyOne's Long Fiber Thermoplastic (LFT) compounds are formulated for demanding applications which require high stiffness and good impact such as metal replacement or other structural applications. These products exhibit enhanced physical and mechanical properties versus standard short fiber products. Benefits of LFT compounds include improved impact strength, elastic modulus, and material strength across wide temperature ranges from subambient to highly elevated. Furthermore, LFT compounds have been shown to offer improved performance in the areas of creep and fatigue performance, improved dimensional stability, and exhibit an exceptional surface finish when compared to traditional highly filled short fiber products.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Длинное углеродное волокно, 20% наполнитель по весу
|
| Формы | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.27 | g/cm³ | ISO 1183 |
| Формовочная усадка-
Поток | 0.10 - 0.20 | % | ISO 294-4 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения 1 | 15400 | MPa | ISO 527-2 |
| Прочность на растяжение (Yield) | 205 | MPa | ISO 527-2 |
| Удлинение при растяжении 2(Break) | 2.0 | % | ISO 527-2 |
| Флекторный модуль | 12000 | MPa | ISO 178 |
| Flexural Strength (Yield) | 270 | MPa | ISO 178 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность | 16 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 45 | kJ/m² | ISO 179 |
| Ударное падение Dart | 15.6 | J | ASTM D5420 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 110 | °C | ISO 75-2/A |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 90 | °C | |
| Время сушки | 8.0 - 12 | hr | |
| Температура обработки (расплава) | 220 - 250 | °C | |
| Температура формы | 80 | °C | |
| Инструкции по впрыску |
|---|
| LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts dependgreatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "lowshear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed.This grade must be dried in a dessicant dryer with a dew point set at -40°C. |
| Примечание |
|---|
| 1 . | Type 1, 5.1 mm/min |
| 2 . | Type 1, 5.1 mm/min |