Описание материалов:
NTX 101 is a hexene copolymer linear low density polyethylene film resin with ultra-high strength. Compared with other hexene copolymers, the film made of NTX 101 has excellent toughness, especially impact strength and tear strength. It can be stably used for blown film extrusion and does not contain a refreshing agent or an opening agent, so it can be well applied to blow-molded wrapping films.
| Главная Информация | |
|---|
| Добавка | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.90 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Сектантный модуль | | | ASTM D882 |
| 1% secant, MD | 163 | MPa | ASTM D882 |
| 1% secant, TD | 183 | MPa | ASTM D882 |
| Прочность на растяжение | | | ASTM D882 |
| MD
: Yield | 9.10 | MPa | ASTM D882 |
| TD
: Yield | 9.38 | MPa | ASTM D882 |
| MD
: Fracture | 62.6 | MPa | ASTM D882 |
| TD
: Fracture | 50.8 | MPa | ASTM D882 |
| Удлинение при растяжении | | | ASTM D882 |
| MD
: Fracture | 630 | % | ASTM D882 |
| TD
: Fracture | 720 | % | ASTM D882 |
| Ударное падение Dart | 330 | g | ASTM D1709A |
| Elmendorf Tear Strength | | | ASTM D1922 |
| MD | 460 | g | ASTM D1922 |
| TD | 600 | g | ASTM D1922 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блеск (45°) | 37 | | ASTM D2457 |
| Haze | 17 | % | ASTM D1003 |
| Юридическое заявление |
|---|
| 有关潜在食品接触应用合规信息（例如：FDA、EU、HPFB），请与埃克森美孚化工客户服务代表联系。本产品不宜在医疗应用中使用，亦不应在任何此类应用中使用 |