LUVOCOM® 1301-VAP 05

Категория	PPS, Polyphenylene Sulfide
Производитель	LEHVOSS Group
Торговая марка	LUVOCOM®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	LGyB9H_LUVOCOM1301VAP05.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOCOM®1301-VAP 05 is a polyphenylene sulfide (PPS) material that contains a carbon fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 1301-VAP 05 are:

Conductivity

Flame Retardant

low viscosity

Good stiffness

Heat resistance

Typical application areas include:

textile/fiber

engineering/industrial accessories

Automotive Industry

business/office supplies

medical/health care

Главная Информация
Наполнитель/армирование	Армированный материал из углеродного волокна
Добавка	Смазка
Характеристики	Проводящий Низкая вязкость Жесткий, хороший Статическая проводимость Теплостойкость, высокая Смазка Огнестойкий
Используется	Текстильные изделия Инженерные аксессуары Применение в автомобильной области Бизнес-оборудование Медицинские принадлежности/принадлежности для ухода
Внешний вид	Темно-серый

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.50	g/cm³	ISO 1183
Формовочная усадка	0.10 - 0.30	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 0.050	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	25000	MPa	ISO 527-2
Tensile Stress (Break)	148	MPa	ISO 527-2
Растяжимое напряжение (Yield)	0.90	%	ISO 527-2
Флекторный модуль	21000	MPa	ISO 178
Флекторный стресс	209	MPa	ISO 178
Flexural Strain at Flexural Strength	1.1	%	ISO 178

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Максимальная рабочая температура- Короткий срок	240	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance		ohms	IEC 60167

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Charpy Unnotched Impact Strength (23°C)	17	kJ/m²	ISO 179/1eU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Heat Deflection Temperature (1.8 MPa, Unannealed)	260	°C	ISO 75-2/A
Температура непрерывного использования	220	°C	UL 746B
Викат Температура размягчения	250	°C	ISO 306/A
Теплопроводность ¹	5.0	W/m/K

Электрический	Номинальное значение	Единица измерения	Метод испытания
Удельное сопротивление поверхности	< 1.0E+2	ohms	IEC 60093

Инъекция	Номинальное значение	Единица измерения
Температура сушки
Hot air dryer	100 - 140	°C
Hot air dryer, B	50 - 90	°C
Время сушки
Hot air dryer	2.0 - 4.0	hr
Hot air dryer, B	> 4.0	hr
Задняя температура	300 - 320	°C
Средняя температура	310 - 330	°C
Передняя температура	320 - 340	°C
Температура сопла	320 - 340	°C
Температура обработки (расплава)	330	°C
Температура формы	150 - 180	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information The material does not necessarily have to be predried; when originally sealed containers are used, this process may normally be omitted. Processing temperatures above 360°C may very rapidly cause thermal damage and should therefore be avoided. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information The material does not necessarily have to be predried; when originally sealed containers are used, this process may normally be omitted. Processing temperatures above 360°C may very rapidly cause thermal damage and should therefore be avoided. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Примечание
1 .	Hot-Disk, 60x60x3 mm

Тип материала	Категория	Производитель
RTP 1305 D	PPS	RTP Company
Lion Idemitsu Composites PPS V170N3	PPS	Lion Idemitsu Composites Co., Ltd.
INSTRUC PPSLGFMIN65	PPS	Infinity LTL Engineered Compounds
LUVOCOM® 1301-0825	PPS	Lehmann & Voss & Co.
Polygen SFG6C-BK	PPS	Shanghai Polygen Science and Technology Co., Ltd.
RTP 1300 C GB 40	PPS	RTP Company

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

