- Alkathene® XJF143
Alkathene® XJF143
| Категория | LLDPE, Linear Low Density Polyethylene |
| Производитель | Qenos Pty Ltd |
| Торговая марка | Alkathene® |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
L0XqXe_Alkathene-XJF143.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
XJF143 is a low density polyethylene designed for a variety of low gauge (20 - 50µm) general purpose film applications. XJF143 does not contain any additives.
XJF143 is intended for use in a variety of general purpose film applications, typically of the thickness 20 to 50µm, and blending into other film grades
XJF143 is intended for use in a variety of general purpose film applications, typically of the thickness 20 to 50µm, and blending into other film grades
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.921 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 32 | µm | |
| Сектантный модуль | ASTM D882 | ||
| 2% secant, MD : 32 µm | 150 | MPa | ASTM D882 |
| 2% secant, TD : 32 µm | 180 | MPa | ASTM D882 |
| Прочность на растяжение | ASTM D882 | ||
| MD : Yield, 32 µm, blown film | 10.0 | MPa | ASTM D882 |
| TD : Yield, 32 µm, blown film | 9.00 | MPa | ASTM D882 |
| MD : Broken, 32 µm | 22.0 | MPa | ASTM D882 |
| TD : Broken, 32 µm | 17.0 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Broken, 32 µm | 290 | % | ASTM D882 |
| TD : Broken, 32 µm | 810 | % | ASTM D882 |
| Ударное падение Dart (32 µm, Blown Film) | 70 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 32 µm, blown film | 420 | g | ASTM D1922 |
| TD : 32 µm | 180 | g | ASTM D1922 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45 °, 32.0 µm, blown film) | 77 | ASTM D2457 | |
| Haze (32.0 µm, blown film) | 5.0 | % | ASTM D1003 |
| Дополнительная информация |
|---|
| Film properties taken from blown film processed at a blow up ratio of 2:1. |
| Тип материала | Категория | Производитель |
|---|---|---|
| PRIMALENE WPP673-01 | LLDPE | Southern Polymer, Inc. |
| SABIC® LLDPE 318BE | LLDPE | Saudi Basic Industries Corporation (SABIC) |
| Bynel® 4105 | LLDPE | DuPont Packaging & Industrial Polymers |
| CERTENE™ LLBD-2024G | LLDPE | Muehlstein |
| Halene L 71601W | LLDPE | Haldia Petrochemicals Ltd. |
| HIFOR Xtreme® SC74853 | LLDPE | Westlake Chemical Corporation |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved